The development and characterization of a hybrid hydrogel based on chitosan (CS) and poly(vinyl alcohol) (PVA) chemically cross-linked with epichlorohydrin (ECH) is presented. The mechanical response of these hydrogels was evaluated by uniaxial tensile tests; in addition, their structural properties such as average molecular weight between cross-link points (M_crl), mesh size (D_N), and volume fraction (v_s) were determined. This was done using the equivalent polymer network theory in combination with the obtained results from tensile and swelling tests. The films showed Young’s modulus values of 11 ± 2 MPa and 9 ± 1 MPa for none irradiated and ultraviolet (UV) irradiated hydrogels, respectively. The cell viability was assessed using Calcein AM and Ethidium homodimer-1 assay and environmental scanning electron microscopy. The 1-(4,5-dimethylthiazol-2-yl)-3,5-diphenylformazan thiazolyl blue formazan (MTT Formazan assay) results did not show cytotoxic effects; this was in good agreement with nuclear magnetic resonance and fourier transform infrared spectroscopies; their results did not show traces of ECH. This indicated that after the crosslinking process, there was no free ECH; furthermore, any possibility of ECH release in the construct during cell culture was discarded. The CS-PVA-ECH hybrid hydrogel allowed cell growth and extracellular matrix formation and showed adequate mechanical, structural, and biological properties for potential use in tissue engineering applications.

Chronic wounds are a global health problem, and their treatments are difficult and long lasting. The development of medical devices through tissue engineering has been conducted to heal this type of wound. In this study, it was demonstrated that the combination of natural and synthetic polymers, such as poly (D-L lactide-co-glycolide) (PLGA) and gelatin (Ge), were useful for constructing scaffolds for wound healing. The aim of this study was to evaluate the influence of different PLGA/gelatin ratios (9:1, 7:3 and 5:5 (v/v)) on the physical, chemical and biological properties of electrospun scaffolds for wound dressings. These PLGA/Ge scaffolds had randomly oriented fibers with smooth surfaces and exhibited distances between fibers of less than 10 μ m. The 7:3 and 5:5 PLGA/Ge scaffolds showed higher swelling, hydrophilicity and degradation rates than pure PLGA and 9:1 (v/v) PLGA/Ge scaffolds. Young’s moduli of the scaffolds were 72 ± 10, 48 ± 6, 58 ± 6 and 6 ± 1 MPa for the pure PLGA scaffold and the 9:1, 7:3 and 5:5 (v/v) PLGA/Ge scaffolds, respectively. Mesenchymal stem cells (MSCs) seeded on all the PLGA/Ge scaffolds were viable, and the cells were attached to the fibers at the different analyzed timepoints. The most significant proliferation rate was observed for cells on the 7:3 PLGA/Ge scaffolds. Biocompatibility analysis showed that all the scaffolds produced inflammation at the first week postimplantation; however, the 7:3 and 5:5 (v/v) PLGA/Ge scaffolds were degraded completely, and there was no inflammatory reaction observed at the fourth week after implantation. In contrast, the 9:1 PLGA/Ge scaffolds persisted in the tissue for more than four weeks; however, at the eighth week, no traces of the scaffolds were found. In conclusion, the scaffolds with the 7:3 PLGA/Ge ratio showed suitable physical, chemical and biological properties for applications in chronic wound treatments.

We demonstrate a new type of smart composite based on carbon soot nanoparticles (CSP) and Poly(dimethylsiloxane). The addition of CSP in this polymeric matrix yields a composite with photomechanical response triggered by IR laser irradiation. The load capacity of this optically driven material ranged between 10 and 16 kPa depending on the CSP concentration in the composites. These photomechanical actuation features promises a good alternative for low-cost smart composite materials for photonic applications such as optically reconfigurable surfaces and optical actuating-sensing devices.