Powder coatings are gaining popularity for their economic and environmental benefits. Additives (pigments) such as zinc phosphate enhance the anti-corrosive properties of coatings, but their behavior in powder coatings has not been extensively studied. In this study, zinc phosphate was incorporated into three powder coating systems: polyester clearcoat, polyester and epoxy coatings with filler BaSO₄. Neutral salt spray and electrochemical tests (OCP, LPR, and EIS) confirmed that the anti-corrosive performance improved with the addition of zinc phosphate. The optimal additive dosage was determined to be 2% for all of the coating systems studied here, based on salt spray tests. Here, the time until failure increased by 1.5 to 2 times. Using electrochemical tests, an optimal additive dosage of 8% was found for the polyester clearcoat, while the other coating systems maintained an optimal additive dosage of 2%. Performance increased by as much as one order of magnitude based on resistance/impedance measurements. This suggested a synergistic effect between the additive and the filler. The passivation layer was confirmed by both X-ray diffraction and Raman spectroscopy. Based on the results and discussion presented in this article, the discrepancy was caused by different features of the two tests, such that the electrochemical tests probe the function of intact coatings, whereas salt spray measures only the corrosion spreading from the scribe. It is proposed that the two test methods characterize different aspects of the coatings, corresponding to their service conditions. This has theoretical and practical significance in the evaluation of anti-corrosive coatings. Other properties of the coatings, including adhesion, gloss, distinctness-of-image, and pencil hardness, were measured as per applicable standards and the conformance was verified.

Ultrafine powder coatings are one of the development directions in the powder coating industry, as they can achieve thin coatings with good leveling and high surface smoothness comparable to liquid coatings. Compared to regular coatings, they experience a higher sensitivity to any incompatibilities, e.g., filler from coating components. The properties of fillers play a great role in the performance of coating films. Aluminum trihydrate (Al(OH)₃) is a well-known filler in solvent-based coatings and other polymer industries. To study and evaluate the performances of Al(OH)₃ in ultrafine powder coatings, a popular filler, barium sulfate (BaSO₄) is used for comparison. Both fillers are added in ultrafine powder coatings based on two of the most commonly used resin systems (polyester-epoxy and polyester). The differences of physical and chemical properties between both fillers have significant influences on several properties of powder paints and coating films. The polar groups (hydrogen bond) in Al(OH)₃ result in the strong interaction between inorganic filler and organic polymer matrix, thus decreasing the molecular network mobility and influencing the chain formation, which is verified by differential scanning calorimetric (DSC). The bed expansion ratio (BERs) of powder paints incorporated with Al(OH)₃ are much higher than those with BaSO₄, which indicate more uniform gas-solid contact during the spraying process. Samples with Al(OH)₃ exhibit much lower specular gloss at 60°, which are expected to achieve remarkable matting effects. Superior corrosion resistances can be observed for almost all the coated panels incorporated with Al(OH)₃ in contrast to those with BaSO₄. Other aspects are slightly influenced by the difference between the two fillers, such as the angle of repose values (AORs) of powder paints, the impact resistance and flexibility of coating films.

Aluminum trihydrate (ATH) is one of the most widely used fillers in solvent-borne coatings and polymer industries. To investigate its performance in powder coatings, four different pigment to binder ratios (P/B) were used in respect to different ATH concentrations in four most widely used resin systems (epoxy, epoxy-polyester, polyurethane and polyester). The angle of repose (AOR) and specific gravity of powder paints increase accordingly with ATH concentration. The mechanical properties, corrosion and UV resistance performances of coating films are enhanced or only slightly decreased with the addition of ATH. Pencil scratch hardness increase significantly with the increase of ATH content. Impact resistance decreases within 5% of the initial resistance at the maximum ATH loading. There is a slightly decrease in corrosion resistance performances of less than 2 mm of failure at scribe in all formulations. The incorporation of ATH has slight effect on the UV resistance performance of all the samples. Moreover, the matting effect of ATH is observed for all the resin systems, especially epoxy, with the specular gloss decreasing more than 70% at P/B of 0.75.

Powder coatings are a promising, solvent-free alternative to traditional liquid coatings due to the superior corrosion protection they provide. This study investigates the effects of incorporating montmorillonite-based nanoclay additives with different particle sizes into polyester/triglycidyl isocyanurate (polyester/TGIC) powder coatings. The objective is to enhance the corrosion-protective function of the coatings while addressing the limitations of commonly employed epoxy-based coating systems that exhibit inferior UV resistance. The anti-corrosive and surface qualities of the coatings were evaluated via neutral salt spray tests, electrochemical measurements, and surface analytical techniques. Results show that the nanoclay with a larger particle size of 18.38 µm (D₅₀, V) exhibits a better barrier effect at a lower dosage of 4%, while a high dosage leads to severe defects in the coating film. Interestingly, the coating capacitance is found, via electrochemical impedance spectroscopy, to decrease during the immersion test, indicating a self-repairing capability of the nanoclay, arising from its swelling and expansion. Neutral salt spray tests suggest an optimal nanoclay dosage of 2%, with the smaller particle size (8.64 µm, D₅₀, V) nanoclay providing protection for 1.5 times as many salt spray hours as the nanoclay with a larger particle size. Overall, incorporating montmorillonite-based nanoclay additives is suggested to be a cost-effective approach for significantly enhancing the anti-corrosive function of powder coatings, expanding their application to outdoor environments.