A method of alumina production based on hydrochloric acid processing of kaolin clays from the East Siberian deposits was studied. Hydrochloric acid leaching was carried out at 160 °C. The leaching solution was subjected to a two-stage crystallization of aluminum chloride hexahydrate (ACH). The precipitated crystals were calcinated in air at a temperature above 800 °C to produce alumina. The main part of water and chlorine during thermal decomposition of ACH was removed at 400 °C. The influence of temperature and duration of ACH calcination on the residual chlorine content in alumina was studied. The optimal temperature of ACH calcination was 900 °C with a duration of 90 min. It was shown that the increase in calcination temperature contributed to the decrease in chlorine content in the final product. However, an increase in calcination temperature above 900 °C led to the transition of the well-soluble γ-Al₂O₃ phase to the insoluble α-Al₂O₃, which negatively affected the further electrolysis of aluminum. The size of alumina particles was not affected by the calcination mode. The rate of dissolution of the prototype Al₂O₃ in Na₃AlF₆ was higher than for the alumina obtained by the classical method. Alumina content, particle morphology, and particle size distribution for the obtained alumina were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), and laser diffraction methods. The obtained alumina is suitable for aluminum production according to the studied characteristics.

Aluminum matrix composites (AMC) are of great interest and importance as high-performance materials with enhanced mechanical properties. Al₂O₃ is a commonly used reinforcement in AMCs fabricated by means of various technological methods, including casting and sintering. Selective laser melting (SLM) is a suitable modern method of the fabrication of net-shape fully dense parts from AMC with alumina. The main results, achievements, and difficulties of SLM applied to AMCs with alumina are discussed in this review and compared with conventional methods. It was shown that the initial powder preparation, namely the particle size distribution, sphericity, and thorough mixing, affected the final microstructure and properties of SLMed materials drastically. The distribution of reinforcing particles tends to consolidate the near-melting pool-edges process because of pushing by the liquid–solid interface during the solidification process that is a common problem of various fabrication methods. The achievement of an homogeneous distribution was shown to be possible through both the thorough mixing of the initial powders and the precise optimization of SLM parameters. The strength of the AMCs fabricated by the SLM method was relatively low compared with materials produced by conventional methods, while for superior relative densities of more than 99%, hardness and tribological properties were obtained, making SLM a promising method for the Al-based matrix composites with Al₂O₃.

The study is devoted to X-ray fluorescence spectroscopy (XRF) features of micro- and nanosized powder mixtures of copper and nickel. XRF is a high accuracy method that allows for both qualitative and quantitative analysis. However, the XRF measurement error due to the size of the studied particles is not usually taken into account, which limits the use of the method in some cases, such as analysis of Ni-Cu mixtures and coatings. In this paper, a method for obtaining copper and nickel nanoparticles was investigated, and the XRF of powder compositions was considered in detail. The initial micro- and nanoparticles of copper and nickel were studied in detail using SEM, TEM, XRD, and EDX. Based on experimental data, calibration curves for copper-nickel powder compositions of various sizes were developed. According to the results, it was experimentally established that the calibration curves constructed for nanoscale and microscale powders differ significantly. The presented approach can be expanded for other metals and particle sizes.

Volumetric cubic and cylindrical samples from MQP-S Nd-Fe-B-type material were 3D-printed using the LPBF technique. Two different scanning strategies were used: the convenient single laser exposure scanning strategy and the newly proposed double scanning strategy aimed at improving the melting process and increasing the density of the synthesized material. Samples with a relative density value higher than 95% were obtained using the new scanning strategy by reducing void volume and cracks. This was achieved by decreasing internal stresses and reducing the tendency to form and propagate cracks. The double scanning strategy of half laser power followed by full power exposure provides higher magnetic properties (both coercive force and remanence). The coercive force increases with energy input decrease, while remanence has inverse dependence.