The effects of cooling rate (CR) on the mechanical properties and precipitation behavior of carbides in H13 steel during quenching process were investigated. The retained austenite tends to be more unstable with increasing CRs, while the martensite increases gradually, based on XRD analyses and EBSD results. The values of hardness are increased, and the elongation along with impact energy is decreased, respectively, at higher CRs. Tensile strength remains above 2.0 GPa. Work hardening rates increase considerably in three samples, suggesting that transformation-induced plasticity effect may take place during the tensile test. Moreover, an increase in yield strength is observed when CR exceeds 15 K s⁻¹, possibly due to a high volume fraction of martensite, decline in average grain size and precipitation of fine carbides. Types of the precipitates acquired were identified by electrolysis and XRD analyses. The results indicate the predominant existence of MC, M₆C and M₇C₃, which are confirmed by SEM-EDS analyses and FactSage thermodynamic calculations. The size, volume and distribution of the carbides were also scrutinized under SEM. It is found that the volume fraction and size of the precipitates both decrease with increasing CRs. Based on these experimental data, an optimum CR for the quenching process could be determined to achieve the desired distribution of carbides, which in turn leads to the enhanced mechanical behaviors.

This study examines the microstructure, mechanical properties, and precipitation behavior of 1000 MPa grade GEN3 steel when subjected to various quenching processes, with a focus on the quench and partition (Q&P) technique. The Q&P-treated samples achieved 1300 MPa tensile strength and demonstrated superior yield strength, attributed to their refined substructure and their large amounts of precipitates. The quenched samples exhibited the thinnest martensite laths due to the highest martensite volume. Despite the as-annealed samples having the smallest grain size, the Q&P treatment resulted in optimal microstructural refinement results and a high dislocation density, reaching 1.15 × 10¹⁵ m⁻². Analysis of the precipitates revealed the presence of V₈C₇, M₇C₃, M₂C, and Ti(C, N) across various heat treatments. The application of the McCall–Boyd method and the Ashby–Orowan correction model indicated that quench and tempered (Q&T) samples contained the largest volume of fine precipitates, contributing to their high yield strengths. These findings offer valuable insights for optimizing heat treatment processes to develop advanced high-strength steels for industrial applications.