With the increasing concerns on the impact of cement production on the environment and the need to protect the environment, the use of mineral additives as cementitious material to partially substitute cement is being considered as an effective option. One of such material is fired clay brick which can be sourced as generated waste from clay brick industry. This has an added advantage of reducing industrial waste and preserving the natural resources. The experimental objective of this study is to examine the possibility of utilizing clay brick waste as partial replacement for Portland cement in concrete. The clay brick was finely ground into powder size, and after grinding, the morphological characterization of the powder materials was carried out using scanning electron microscopy (SEM). Moreover, the chemical composition of the brick material was determined using X-ray fluorescence (XRF). Laboratory tests were carried out to determine the workability, split tensile and compressive strength properties of the concrete with 0%, 10%, 20%, 30% and 40% partial replacement of cement with ground clay brick (CB). From the test results, the chemical composition of the brick powder meets the standard requirements for pozzolanic material, with the SEM revealing an amorphous solid mass. The workability of the concrete reduces with increase in brick powder content. A significant improvement of the split tensile and compressive strength of the concrete was achieved at 10% cement replacement, after which a decrease in strength with increasing ground clay brick content was recorded. The use of ground clay brick of not more than 15% was recommended for concrete production.

The sustainable benefits of waste glass usage in concrete include the possibility of reducing solid waste and greenhouse gas emission and preservation of raw materials. This current study examines the effect of recycled waste glass as a partial and complete substitute for natural sand in producing eco-friendly concrete. The recycled waste glass was proportioned in levels of 25, 50, 75 and 100% by weight to substitute sand in the concrete using a mix ratio of 1:2:4 (cement:sand:gravel) at a W/C ratio of 0.5 targeting 20 MPa strength at 28 days. Tests, which include X-ray fluorescence (XRF), were conducted on the waste glass and cement materials; slump test was performed on the freshly prepare concrete at different percentage glass content. Compressive and tensile strength tests were performed on 60 specimens after 3, 7, 28 and 90 days of curing. The concrete microstructure was examined using the scanning electron microscope (SEM). Results showed that workability and the mechanical strength of the concrete produced decreased with increasing waste glass content. However, concrete containing 25% and 50% waste glass contents showed significant enhancement in strength, but it is recommended that the optimum glass content should be 25% for the production of sustainable eco-concrete.

Use of waste materials in concrete is now a global trend for efficient waste management so as to achieve a sustainable green environment and with the added advantages of preserving the natural resources as well as producing a better performing concrete. This study examined the properties of concrete containing ground waste glass powder (GP) as partial replacement for cement. The waste glass was finely grounded into powder and the morphology imagery of the powder materials was carried out using scanning electron microscopy (SEM). Moreover, the chemical composition of the glass powdered material was determined using X-ray fluorescence (XRF). Laboratory tests were carried out to determine the strength activity index, workability, split tensile and compressive strength properties of the concrete with 0%, 15%, 18%, 21%, 24%, 27% and 30% partial replacement of cement with the ground waste glass powder. The results showed that the oxides composition of the glass powder meets the requirements for pozzolanic material, while the SEM morphology shows materials of amorphous flaky solid masses, and based on the 28-day strength activity index, concrete containing 21% cement replacement shows a higher strength index above therecommended 75%. It was also observed that workability of the concrete reduced with increase in percentage glass content while significant improvement of the compressive strength of the concrete was achieved at 21% cement replacement, after which a decrease in strength with increasing percentage glass content was observed. The revealed results were confirmed by the microstructural examination using SEM showing a denser concrete at 21% cement replacement but increase porosityas the glass content increases. However, a decrease in split tensile strength was observed with increasing glass content. The results clearly showed that it is possible to produce moderate strength sustainable concrete for structural application using 20% glass powder as cement replacement.

This paper examines the effect of combined bamboo fibers and limestone powder used as filler material on the fresh, hardened and microstructural properties of self-compacting concrete (SCC). The bamboo fibers of aspect ratio (l/d) of 50 and a maximum length of 50 mm was varied in steps of 0.25%, 0.5%, 0.75% and 1% in the SCC mix. While 10% of limestone powder was added as a filler in each of the SCC mix. The workability of the mix was assessed by slump flow test and V-funnel test, while the mechanical properties were assessed by considering the compressive and split tensile strength test after 7, 14 and 28 curing age. All concrete mixes were carried out by following the European Federation for Specialist Construction Chemicals and Concrete (EFNARC) standard, while the microstructure of selected samples was assessed using the Scanning Electron Microscopy (SEM). Test results indicate that fiber addition influences the fresh properties of SCC. Moreover, it was observed that SCC mix containing with fiber content of 0.75% and 0.5% with the inclusion of 10% limestone powder achieved the highest compressive and split tensile strength values of 28.04 MPa and 3.26 MPa, respectively. The result showed an increment of 17.4% and 32% compare to the control mix. Results of SEM showed an improvement in the morphology of the concrete. Hence, bamboo fiber and limestone powder can be sustainably combined to regulate the flow-ability and improving the strength of the self-compacting concrete for local structural construction.