Unidirectional glass fiber reinforced polymer (GFRP) is tested at four initial strain rates (25, 50, 100 and 200 s⁻¹) and six temperatures (−25, 0, 25, 50, 75 and 100 °C) on a servo-hydraulic high-rate testing system to investigate any possible effects on their mechanical properties and failure patterns. Meanwhile, for the sake of illuminating strain rate and temperature effect mechanisms, glass yarn samples were complementally tested at four different strain rates (40, 80, 120 and 160 s⁻¹) and varying temperatures (25, 50, 75 and 100 °C) utilizing an Instron drop-weight impact system. In addition, quasi-static properties of GFRP and glass yarn are supplemented as references. The stress–strain responses at varying strain rates and elevated temperatures are discussed. A Weibull statistics model is used to quantify the degree of variability in tensile strength and to obtain Weibull parameters for engineering applications.

This work presents a method to produce structural composites capable of energy storage. They are produced by integrating thin sandwich structures of CNT fiber veils and an ionic liquid-based polymer electrolyte between carbon fiber plies, followed by infusion and curing of an epoxy resin. The resulting structure behaves simultaneously as an electric double-layer capacitor and a structural composite, with flexural modulus of 60 GPa and flexural strength of 153 MPa, combined with 88 mF/g of specific capacitance and the highest power (30 W/kg) and energy (37.5 mWh/kg) densities reported so far for structural supercapacitors. In-situ electrochemical measurements during 4-point bending show that electrochemical performance is retained up to fracture, with minor changes in equivalent series resistance for interleaves under compressive stress. En route to improving interlaminar properties we produce grid-shaped interleaves that enable mechanical interconnection of plies by the stiff epoxy. Synchrotron 3D X-ray tomography analysis of the resulting hierarchical structure confirms the formation of interlaminar epoxy joints. The manuscript discusses encapsulation role of epoxy, demonstrated by charge-discharge measurements of composites immersed in water, a deleterious agent for ionic liquids. Finally, we show different architectures free of current collector and electrical insulators, in which both CNT fiber and CF act as active electrodes.