OBJECTIVE: A systematic review on nickel-titanium wires was performed. The strategy was focused on Entrez-PubMed-OLDMEDLINE, Scopus and BioMed Central from 1963 to 2008. METHODS: Papers in English and French describing the behavior of these wires and laboratorial methods to identify crystalline transformation were considered. A total of 29 papers were selected. RESULTS: Nickel-titanium wires show exceptional features in terms of elasticity and shape memory effects. However, clinical applications request a deeper knowledge of these properties in order to allow the professional to use them in a rational manner. In addition, the necessary information regarding each alloy often does not correspond to the information given by the manufacturer. Many alloys called "superelastic" do not present this effect; they just behave as less stiff alloys, with a larger springback if compared to the stainless steel wires. CONCLUSIONS: Laboratory tests are the only means to observe the real behavior of these materials, including temperature transition range (TTR) and applied tensions. However, it is also possible to determine in which TTR these alloys change the crystalline structure

Role of plasma nitriding temperature and time in the corrosion behaviour and microstructure evolution of 15-5 PH stainless steel

A comparative study on the mechanical properties, scratch resistance, and localized corrosion (pitting and crevice) of plasma-nitrided Inconel alloy 718 (UNS NO7718: IN 718) was carried out. Thermochemical treatment was performed at low temperatures (400 and 450 °C) for 4 h. The treatment formed layers with thicknesses of 7.17 ± 0.89 µm (400 °C) and 7.96 ± 0.48 µm (450 °C). The XRD and nanohardness analyses indicated the formation of a hard layer composed of the expanded austenite phase (γ_N), CrN at 400 °C, and CrN + γ at 450 °C, with a maximum indentation hardness of 12 and 12.5 GPa, respectively, when compared to the 5 GPa substrate hardness. The scratching tests (2–8 N) showed that with increasing load, the nitrided surfaces had a transition from 100% microcutting to a combination of microplowing/cutting, with the presence of cracks. The critical load of the nitrided surfaces was 3 N for 400 °C and 4 N for 450 °C. The untreated condition maintained a crack-free combined mechanism regardless of the load. For the same load, the nitrided surfaces held lower coefficient of friction values and higher scratch resistance values, which were more pronounced at 450 °C. The linear polarization tests (3.56 wt.% NaCl) showed pitting corrosion in all samples, with the 450 °C condition being less resistant. Nitriding at 400 °C increased the crevice corrosion resistance of Inconel, while at 450 °C, it severely damaged it. Nitriding at 400 °C brought concomitant gains in hardness and scratch and crevice corrosion resistance when compared to the as-received IN 718.