Traditional wood-based panels are produced with synthetic, formaldehyde-based adhesives, commonly made from fossil-derived constituents, such as urea, phenol, melamine, etc. Along with their numerous advantages, such as chemical versatility, high reactivity and excellent adhesive performance, these adhesives are characterized by certain problems, connected with the hazardous volatile organic compounds (VOCs), mostly free formaldehyde in the adhesives and the formaldehyde emission from the finished wood composites, which is carcinogenic to humans and harmful to the environment. The growing environmental concerns and stringent legislative requirements to the formaldehyde emission from wood-based panels have posed new challenges to researchers and industrial practice, related to the development of sustainable, eco-friendly wood-based panels with close-to-zero formaldehyde emission. The most common methods to reduce the formaldehyde emission from wood-based panels have been to decrease the free formaldehyde in the adhesive by modifying the adhesive (like lowering the molar ratio of formaldehyde to urea in UF resin) or by using formaldehyde scavengers, one group of scavengers being for adhesives by mixing or reacting and the second one scavengers for wood-based panels as post-treatments. Another way is to use alternative bio-based adhesives, however, there are still substantial challenges for the complete replacement of formaldehyde-based adhesives with bio-based adhesives, mainly because of their relatively low bonding strength, poor water resistance, etc. This article presents a review and analysis of the current state of research in the field of low formaldehyde emission wood adhesives and formaldehyde scavengers for manufacturing low-toxic, eco-friendly wood composites.

Biocomposites reinforced with natural fibers represent an eco-friendly and inexpensive alternative to conventional petroleum-based materials and have been increasingly utilized in a wide variety of industrial applications due to their numerous advantages, such as their good mechanical properties, low production costs, renewability, and biodegradability. However, these engineered composite materials have inherent downsides, such as their increased flammability when subjected to heat flux or flame initiators, which can limit their range of applications. As a result, certain attempts are still being made to reduce the flammability of biocomposites. The combustion of biobased composites can potentially create life-threatening conditions in buildings, resulting in substantial human and material losses. Additives known as flame-retardants (FRs) have been commonly used to improve the fire protection of wood and biocomposite materials, textiles, and other fields for the purpose of widening their application areas. At present, this practice is very common in the construction sector due to stringent fire safety regulations on residential and public buildings. The aim of this study was to present and discuss recent advances in the development of fire-resistant biocomposites. The flammability of wood and natural fibers as material resources to produce biocomposites was researched to build a holistic picture. Furthermore, the potential of lignin as an eco-friendly and low-cost FR additive to produce high-performance biocomposites with improved technological and fire properties was also discussed in detail. The development of sustainable FR systems, based on renewable raw materials, represents a viable and promising approach to manufacturing biocomposites with improved fire resistance, lower environmental footprint, and enhanced health and safety performance.

This review article aims to summarize the potential of using renewable natural resources, such as lignin and tannin, in the preparation of NIPUs for wood adhesives. Polyurethanes (PUs) are extremely versatile polymeric materials, which have been widely used in numerous applications, e.g., packaging, footwear, construction, the automotive industry, the lighting industry, insulation panels, bedding, furniture, metallurgy, sealants, coatings, foams, and wood adhesives. The isocyanate-based PUs exhibit strong adhesion properties, excellent flexibility, and durability, but they lack renewability. Therefore, this study focused on the development of non-isocyanate polyurethane lignin and tannin resins for wood adhesives. PUs are commercially synthesized using polyols and polyisocyanates. Isocyanates are toxic, costly, and not renewable; thus, a search of suitable alternatives in the synthesis of polyurethane resins is needed. The reaction with diamine compounds could result in NIPUs based on lignin and tannin. The research on bio-based components for PU synthesis confirmed that they have good characteristics as an alternative for the petroleum-based adhesives. The advantages of improved strength, low curing temperatures, shorter pressing times, and isocyanate-free properties were demonstrated by lignin- and tannin-based NIPUs. The elimination of isocyanate, associated with environmental and human health hazards, NIPU synthesis, and its properties and applications, including wood adhesives, are reported comprehensively in this paper. The future perspectives of NIPUs’ production and application were also outlined.

Forest covers 4.06 billion hectares (ha) or 31 of the total land area worldwide, where 93 (3.75 billion ha) are natural regenerating forests and the remaining 7 (294 million ha) are planted forests. Eucalyptus spp., being one of the most important plantation species, has been planted in 95 countries around the world, and the area of plantation has exceeded 22.57 million ha. In the southern hemisphere, it is a significant industrial fast-growing tree species. These plantations serve as a valuable resource for the timber and fibre-based industries. Eucalyptus is the main fibre resource for the pulp and paper industries in developed countries. Timber extracted from the planted eucalyptus trees has long been used for solid wood and its fibres were used for manufacturing medium-density fibreboard. In comparison to most softwood species, Eucalyptus timber is reported to have a higher rigidity, making it ideal for manufacturing structural products. Therefore, this paper presents a review and analysis of the recent state of research on the utilisation of planted eucalyptus for engineered wood products (EWPs) manufacturing. This study investigated Eucalyptus-based EWPs such as particleboard, fibreboard, oriented strand board, laminated veneer lumber, plywood, glue laminated lumber, and cross-laminated lumber. The feasibility of using planted Eucalyptus in the production of EWPs, as well as the challenges encountered, was also discussed.

The potential of using ground birch (Betula verrucosa Ehrh.) bark as an eco-friendly additive in urea-formaldehyde (UF) adhesives for plywood manufacturing was investigated in this work. Five-ply plywood panels were fabricated in the laboratory from beech (Fagus sylvatica L.) veneers bonded with UF adhesive formulations comprising three addition levels of birch bark (BB) as a filler (10%, 15%, and 20%). Two UF resin formulations filled with 10% and 20% wheat flour (WF) were used as reference samples. The mechanical properties (bending strength, modulus of elasticity and shear strength) of the laboratory-fabricated plywood panels, bonded with the addition of BB in the adhesive mixture, were evaluated and compared with the European standard requirements (EN 310 and EN 314-2). The mechanical strength of the plywood with the addition of BB in the adhesive mixture is acceptable and met the European standard requirements. Markedly, the positive effect of BB in the UF adhesive mixture on the reduction of formaldehyde emission from plywood panels was also confirmed. Initially, the most significant decrease in formaldehyde release (up to 14%) was measured for the plywood sample, produced with 15% BB. After four weeks, the decrease in formaldehyde was estimated up to 51% for the sample manufactured with 20% BB. The performed differential scanning calorimetry (DSC), thermal gravimetric analysis (TGA), and derivative thermogravimetry (DTG), also confirmed the findings of the study. As this research demonstrated, BB as a waste or by-product of wood processing industry, can be efficiently utilized as an environmentally friendly, inexpensive alternative to WF as a filler in UF adhesive formulations for plywood manufacturing.