Single-shade universal resin composites (SsURC) are preferred in clinical practice to reduce time for shade selection and obtain good esthetic results. In this study, the static mechanical properties of seven new SsURCs were investigated, their spectral analyzes were performed and scanning electron microscopy (SEM) evaluations were presented. Charisma Diamond One/DO, Admira Fusion x-tra/AFX, Omnichroma/OC, OptiShade/OS, Essentia Universal/EU, Zenchroma/ZC, Vittra APS Unique/VU were used in a three-point bending test to determine flexural strength (F_S) and elastic modulus (E_M); Vickers micro-hardness (VHN) and hardness-ratio (HR) were performed with a micro-hardness tester from top/bottom after 24-h/15-days of storage in distilled water at 37 °C (±1 °C). The degree of conversion (DC) was assessed by using Fourier transform infrared spectroscopy (FTIR). The structure of the resin matrix and filler content were assessed by SEM. Data were analyzed using IBM SPSS V23 and the R program and the significance level was taken as p < 0.05. The main effect of the tested SsURCs was found to be statistically significant on F_S, E_M, VHN, and DC values (p < 0.001). Bis-GMA free SsURCs (AFX, DO, VU) showed better DC and HR except for OC. All seven tested SsURCs conform to the requirements of ISO standards for dental resin composites for all tested categories.

The effect of bleaching on enamel surfaces, as well as exploring methods of preventing the weakening of bond strength of two different adhesives to bleached enamel surfaces. This study compared the shear bond strength (SBS) of two different adhesives on bleached enamel immediately after bleaching, with a 1-week delay, and following application of an antioxidizing agent after bleaching. Materilas and Method: The enamel surfaces of 140 incisors were divided into 14 groups. Two unbleached enamel groups (n = 20) were prepared as negative controls of the Adper Single Bond 2 total-etch and Clearfil Tri S Bond self-etch adhesives. The remaining surfaces were randomly divided into two bleaching groups treated with 35% Beyond Max (n = 60) and 38% Opalescence Xtra Boost (n = 60). Each bleaching group was then divided into two subgroups using the total and self-etch adhesive systems. Specimens were bonded immediately after bleaching, after treatment with 10% sodium ascorbate (SA) gel, or after 1-week of immersion in artificial saliva. All groups were restored with composite resin. After thermocycling, SBS was measured and data were analyzed. In the control groups, there was no statistically-significant difference in SBS between self-and total-etch adhesives. Among all bleaching groups, no statistically-significant differences in SBS were noted, although the SA-treated delayed bonding (1-week) groups had the highest values. The lowest values were noted for the groups bonded immediately after bleaching.

The aim of this study is to determine the cytotoxicity of three different nano composite resins (CRs) on human gingival fibroblast (hGF) and periodontal ligament fibroblast (hPDLF) cell lines. These CRs selected were nanohybrid organic monomer-based Admira Fusion (AF), nanohybrid Bis-(acryloyloxymethyl) tricyclo [5.2.1.0.sup.2,6] decane-based Charisma Topaz (CT), and supra nano filled resin-based Estelite Quick Sigma (EQS). MTT assay was performed to assess the cytotoxicity of CRs at 24 h and one week. AF and EQS applied on hGF cells at 24 h and one week demonstrated similar cytotoxic outcomes. Cytotoxicity of CT on hGF cells at one week was higher than 24 h (p = 0.04). Cytotoxicity of CT on hGF cells was higher at 24 h (p = 0.002) and one week (p = 0.009) compared to control. All composites showed higher cytotoxicity on hPDLF cells at one week than the 24 h (AF; p = 0.02, CT; p = 0.02, EQS; p = 0.04). AF and EQS demonstrated lower cytotoxicity on hPDLF cells than the control group at 24 h (AF; p = 0.01, EQS; p = 0.001). CT was found more cytotoxic on hPDLF cells than the control (p = 0.01) and EQS group (p = 0.008) at one week. The cytotoxicity of CRs on hGF and hPDLF cells vary, according to the type of composites, cell types, and exposure time.

The use of multivitamins has become widespread globally, yet there is a scarcity of studies investigating their impact on resin composite restorations. This study aimed to evaluate the effect of an effervescent multivitamin tablet on micro-hybrid dental resin composites’ surface roughness and color. Fifty disc-shaped samples (8 × 2 mm, shade A2; n = 10) were prepared and polished using five different micro-hybrid resin composites (Pergamon, Dentac, Turkey; Estelite Posterior, Tokuyama, Japan; Geanial Anterior, GC, Japan; Charisma Opal, Kulzer, Germany; Beautifil II, Shofu, USA). Samples were immersed in 200 mL water to one effervescent multivitamin tablet (Redoxon Triple Action, Bayer) at 24 °C for 2 min a day in 24 h intervals for 30 days. All samples’ surface roughness (Ra) and ΔE(L*a*b) measurements were recorded at the beginning and end of the 30 days. The Wald chi-square and a two-way ANOVA were used for statistical analysis (significance level p < 0.05). The resin composite type and exposure to the multivitamin had a statistically significant effect on Ra values (p < 0.05). The resin composite type had a statistically significant effect on ΔE values, likely due to the higher mean value of BII (p = 0.040). The surface roughness and color of resin composites can be affected by multivitamins with a pH value of 3.0. Therefore, it is important to consider the patient’s routine vitamin intake during resin composite selection. Additional research is required to explore the properties of different dental restorative materials.