The methoxy-type silane coupling agents were synthesized via the modification of the hydrolyzable group and characterized to investigate the change in properties of silica/rubber composites based on the different silane coupling agent structures and the masterbatch fabrication methods. The prepared methoxy-type silane coupling agents exhibited higher reactivity towards hydrolysis compared to the conventional ethoxy-type one which led to the superior silanization to the silica filler surface modified for the reinforcement of styrene-butadiene rubber. The silica/rubber composites based on these methoxy-type silane coupling agents had the characteristics of more developed vulcanization and mechanical properties when fabricated as masterbatch products for tread materials of automobile tire surfaces. In particular, the dimethoxy-type silane coupling agent showed more enhanced rubber composite properties than the trimethoxy-type one, and the environmentally friendly wet masterbatch fabrication process was successfully optimized. The reactivity of the synthesized silane coupling agents toward hydrolysis was investigated by FITR spectroscopic analysis, and the mechanical properties of the prepared silica-reinforced rubber polymers were characterized using a moving die rheometer and a universal testing machine.

Lift-off is one of the last steps in the production of next-generation flexible electronics. It is important that this step is completed quickly to prevent damage to ultrathin manufactured electronics. This study investigated the chemical structure of polyimide most suitable for the Xe Flash lamp–Lift-Off process, a next-generation lift-off technology that will replace the current dominant laser lift-off process. Based on the characteristics of the peeled-off polyimide films, the Xe Flash lamp based lift-off mechanism was identified as photothermal decomposition. This occurs by thermal conduction via light-to-heat conversion. The synthesized polyimide films treated with the Xe Flash lamp–Lift-Off process exhibited various thermal, optical, dielectric, and surface characteristics depending on their chemical structures. The polyimide molecules with high concentrations of –CF₃ functional groups and kinked chemical structures demonstrated the most promising peeling properties, optical transparencies, and dielectric constants. In particular, an ultra-thin polyimide substrate (6 μm) was successfully fabricated and showed potential for use in next-generation flexible electronics.

Conventional fluorescent dyes have the property of decreasing fluorescence due to aggregation-caused quenching effects at high concentrations, whereas aggregation-induced emission dyes have the property of increasing fluorescence as they aggregate with each other. In this study, diketopyrrolopyrrole-based long-wavelength aggregation-induced emission dyes were used to prepare biocompatible nanoparticles suitable for bioimaging. Aggregation-induced emission nanoparticles with the best morphology and photoluminescence intensity were obtained through a fast, simple preparation method using an ultrasonicator. The optimally prepared nanoparticles from 3,6-bis(4-((E)-4-(bis(40-(1,2,2-triphenylvinyl)-[1,10-biphenyl]-4-yl)amino)styryl)phenyl)-2,5-dihexyl-2,5-dihydropyrrolo[3,4-c]pyrrole-1,4-dione (DP-R2) with two functional groups having aggregation-induced emission properties and additional donating groups at the end of the triphenylamine groups were considered to have the greatest potential as a fluorescent probe for bioimaging. Furthermore, it was found that the tendency for aggregation-induced emission, which was apparent for the dye itself, became much more marked after the dyes were incorporated within nanoparticles. While the photoluminescence intensities of the dyes were observed to decrease rapidly over time, the prepared nanoparticles encapsulated within the biocompatible polymers maintained their initial optical properties very well. Lastly, when the cell viability test was conducted, excellent biocompatibility was demonstrated for each of the prepared nanoparticles.