Lithium-Ion Batteries (LIBs) usually present several degradation processes, which include their complex Solid-Electrolyte Interphase (SEI) formation process, which can result in mechanical, thermal, and chemical failures. The SEI layer is a protective layer that forms on the anode surface. The SEI layer allows the movement of lithium ions while blocking electrons, which is necessary to prevent short circuits in the battery and ensure safe operation. However, the SEI formation mechanisms reduce battery capacity and power as they consume electrolyte species, resulting in irreversible material loss. Furthermore, it is important to understand the degradation reactions of the LIBs used in Electric Vehicles (EVs), aiming to establish the battery lifespan, predict and minimise material losses, and establish an adequate time for replacement. Moreover, LIBs applied in EVs suffer from two main categories of degradation, which are, specifically, calendar degradation and cycling degradation. There are several studies about battery degradation available in the literature, including different degradation phenomena, but the degradation mechanisms of large-format LIBs have rarely been investigated. Therefore, this review aims to present a systematic review of the existing literature about LIB degradation, providing insight into the complex parameters that affect battery degradation mechanisms. Furthermore, this review has investigated the influence of time, C-rate, depth of discharge, working voltage window, thermal and mechanical stresses, and side reactions in the degradation of LIBs.

Greenhouse gas emissions from transportation harm the environment. In response to these environmental concerns, numerous countries encourage the adoption of electric vehicles (EVs) as a more environmentally friendly option than traditional gasoline-powered vehicles. Advances in battery technology have made batteries an alternative solution for energy storage in stationary applications and for electric mobility. Reduced lithium-ion batteries (LIBs) production costs due to economies of scale, electrode material and cell design developments, and manufacturing process improvements have driven this success. This trend is expected to increase the number of LIBs on the market that may be discarded in the environment at the end of their useful life if more sustainable alternatives are not technologically mature. This coming environmental concern can be mitigated by collecting wasted EV batteries, reconfiguring them, and reusing them for applications with less stringent weight, performance, and size requirements. This method would extend battery life and reduce environmental effects. The present work investigates the main regulatory structures of the second-life battery industry that require rules, technical standards, and laws. To achieve this objective, a systematic review was carried out following a strict protocol that includes identifying relevant studies, extracting data and information, evaluating, and summarizing information. This paper explains the primary rules and technical standards governing the second-life battery business. The findings highlight the need for universities, research institutions, and government agencies to evaluate the second-life battery industry objectively. This would enable the creation of new technological regulations and laws for this burgeoning industry.

Fused Deposition Modeling (FDM) is a well-established manufacturing method for producing both prototype and functional components. This study investigates the mechanical properties of FDM components by material and process-related influencing variables. Tensile tests were conducted on seven different materials in their raw filament form, two of which were fiber-reinforced, to analyze their material-related influence. To cover a wide range from standard to advanced materials relevant for load-carrying components as well as their respective variations, polylactic acid (PLA), 30% wood-fiber-reinforced PLA, acrylonitrile butadiene styrene (ABS), polycarbonate (PC), a blend of ABS and PC, Nylon, and 30% glass-fiber-reinforced Nylon were selected. The process-related influencing variables were studied using the following process parameters: layer thickness, nozzle diameter, build orientation, nozzle temperature, infill density and pattern, and raster angle. The first test series revealed that the addition of wood fibers significantly worsened the mechanical behavior of PLA due to the lack of fiber bonding to the matrix and significant pore formation. The polymer blend of ABS and PC only showed improvements in stiffness. Significant strength and stiffness improvements were found by embedding glass fibers in Nylon, despite partially poor fiber–matrix bonding. The materials with the best properties were selected for the process parameter analysis. When examining the impact of layer thickness on part strength, a clear correlation was evident. Smaller layer thicknesses resulted in higher strength, while stiffness did not appear to be affected. Conversely, larger nozzle diameters and lower nozzle temperatures only positively impacted stiffness, with little effect on strength. The part orientation did alter the fracture behavior of the test specimens. Although an on-edge orientation resulted in higher stiffness, it failed at lower stresses. Higher infill densities and infill patterns aligned with the load direction led to the best mechanical results. The raster angle had a significant impact on the behavior of the printed bodies. An alternating raster angle resulted in lower strengths and stiffness compared to a unidirectional raster angle. However, it also caused significant stretching due to the rotation of the beads.

The fatigue behavior of a cellular composite with an epoxy matrix and glass foam granules is analyzed and modeled by means of continuum damage mechanics. The investigated cellular composite is a particular type of composite foam, and is very similar to syntactic foams. In contrast to conventional syntactic foams constituted by hollow spherical particles (balloons), cellular glass, mineral, or metal place holders are combined with the matrix material (metal or polymer) in the case of cellular composites. A microstructural investigation of the damage behavior is performed using scanning electron microscopy. For the modeling of the fatigue behavior, the damage is separated into pure static and pure cyclic damage and described in terms of the stiffness loss of the material using damage models for cyclic and creep damage. Both models incorporate nonlinear accumulation and interaction of damage. A cycle jumping procedure is developed, which allows for a fast and accurate calculation of the damage evolution for constant load frequencies. The damage model is applied to examine the mean stress effect for cyclic fatigue and to investigate the frequency effect and the influence of the signal form in the case of static and cyclic damage interaction. The calculated lifetimes are in very good agreement with experimental results.