Primary and secondary intragranular austenite precipitation and its relationship with chromium nitride (Cr₂N) were studied in a simulated multipass heat affected zone (HAZ) of five duplex stainless steel alloys (UNS S32304, S32205, S32550, S32750, and S32760). The Gleeble thermal-mechanical simulator was used to perform short duration and high cooling rate ferritisation and reheating heat treatments. TEM and FEG-SEM analysis, coupled with a specially developed electrolytic etching technique, revealed the cooperative growth of secondary austenite and Cr₂N precipitation along the ferrite/austenite (α/γ) interfaces. Additionally, the observed close coexistence of intragranular nitride (Cr₂N) and intragranular secondary austenite suggests the heterogeneous nucleation of secondary austenite from the nitrides as supported by previously reported low energy nitride/austenite (Cr₂N/γ) interfaces for the observed orientation relationship between both phases. Based on these observations, a new mechanism is proposed for intragranular secondary austenite nucleation related to the intragranular nitride precipitates.

Mechanical properties of welded joints depend on the way heat flows through the welding passes. In multipass welding the reheating of the heat affected zone (HAZ) can form local brittle zones that need to be delimited for evaluation. The difficulty lies in the choice of a model that can simulate multipass welding. This study evaluated Rosenthal’s Medium Thick Plate (MTP) and the Distributed heat Sources (DHS) of Mhyr and Gröng models. Two assumptions were considered for both models: constant and temperature-dependent physical properties. It was carried out on a multipass welding of an API 5L X80 tube, with 1016 mm (42″) external diameter, 16 mm thick and half V-groove bevel, in the 3G up position. The root pass was welded with Gas Metal Arc Welding (GMAW) process with controlled short-circuit transfer. The Flux Cored Arc Welding (FCAW) process was used in the filling and finishing passes, using filler metal E111T1-K3M-JH4. The evaluation criteria used were overlapping the simulated isotherms on the marks revealed in the macrographs and the comparison between the experimental thermal cycle and those simulated by the proposed models. The DHS model with the temperature-dependent properties presented the best results and simulated with accuracy the HAZ of root and second welding passes. In this way, it was possible to delimit the HAZ heated sub-regions.