The as-synthesized TiO₂ nanorods a-TNR (amorphous TiO₂ layer covering the crystalline anatase TiO₂ core) and TNR (fully crystalline anatase TiO₂) were decorated with reduced graphene oxide (rGO) to synthesize two series of TiO₂ + rGO composites with different nominal loadings of GO (from 4 to 20 wt%). The structural, surface and electronic properties of the obtained TiO₂ + rGO composites were analyzed and correlated to their performance in the photocatalytic oxidation of aqueous bisphenol A solution. X-ray photoelectron spectroscopy (XPS) analyses revealed that charge separation in TiO₂ + rGO composites is improved due to the perfect matching of TiO₂ and rGO valence band maxima (VBM). Cyclic voltammetry (CV) experiments revealed that the peak-to-peak separations (ΔE_p) are the lowest and the oxidation current densities are the highest for composites with a nominal 10 wt% GO content, meaning that it is much easier for the charge carriers to percolate through the solid, resulting in improved charge migration. Due to the high charge carrier mobility in rGO and perfect VBM matching between TiO₂ and rGO, the electron–hole recombination in composites was suppressed, resulting in more electrons and holes being able to participate in the photocatalytic reaction. rGO amounts above 10 wt% decreased the photocatalytic activity; thus, it is critical to optimize its amount in the TiO₂ + rGO composites for achieving the highest photocatalytic activity. BPA degradation rates correlated completely with the results of the CV measurements, which directly evidenced improved charge separation and migration as the crucial parameters governing photocatalysis.

We have determined the Schottky barrier height (0.23 eV) and efficient photoelectron generation in novel multisegmented Au/TiO₂ nanorod arrays.