Graphene oxide (GO), reduced graphene oxide by thermal treatment (rGO-TT), nitrogen-modified rGO (N-rGO), and carbon Vulcan were synthesized and employed in the current work as catalyst support for Pt nanoparticles, to study their properties and impact toward the methanol oxidation reaction (MOR) in sulfuric acid medium. Several physicochemical techniques, such as X-ray photoelectron spectroscopy (XPS), X-ray powder diffraction (XRD), Transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDX), Raman, and elemental analysis were employed to characterize the novel materials, while potentiodynamic and potentiostatic methods were used to study catalytic performance toward the methanol oxidation reaction in acidic medium. The main results indicate a high influence of the support on the surface electronic state of the catalyst, and consequently the catalytic performance toward the MOR is modified. Accordingly, Pt/N-rGO and Pt/rGO-TT show the lowest and the highest catalytic performance toward the MOR, respectively.

In this work, Ni nanoparticles (NPs), with nominal metallic loading of 20 wt%, were deposited on graphene-based materials (GMs) doped with nitrogen and sulphur, in order to study their electrocatalytic activity towards the oxygen reduction reaction (ORR) and hydrogen evolution reaction (HER) in alkaline medium. Different chemical reducing agents were employed to synthesize the catalysts. Results indicate that the presence of heteroatoms in the GMs influences the activity of both the GMs and the Ni-based catalysts. Thus, best results were obtained for catalyst containing nitrogen and sulphur for the ORR which favours the direct four-electron pathway, whereas for the HER, the highest performance was observed for N-doped materials.

Ni nanoparticles supported on graphene-based materials were tested as catalysts for the oxygen reduction reaction (ORR) to be used in anion exchange membrane fuel cells (AEMFCs). The introduction of N into the graphene structure produced an enhancement of electrocatalytic activity by improving electron transfer and creating additional active sites for the ORR. Materials containing both N and S demonstrated the highest stability, showing only a 3% performance loss after a 10 h stability test and therefore achieving the best overall performance. This long-term durability is attributed to the synergetic effect of Ni nanoparticles and bi-doped (S/N)-reduced graphene oxide. The findings suggest that the strategic incorporation of both nitrogen and sulphur into the graphene structure plays a crucial role in optimising the electrocatalytic properties of Ni-based catalysts.

The development of energy-related materials is crucial to reach efficient energy devices and overcome the increasing global energy demands. Over the past two decades, graphene-based materials have demonstrated to be a promising material in many fields owing to their exceptional properties such as a large surface area, high conductivity and good chemical and thermal stability. For this reason, they have been widely studied for energy conversion and energy storage devices such as electrolyzers, fuel cells, lithium-ion batteries, supercapacitors and photovoltaic cells. In this chapter, significant advances for the recently graphene-based materials developed for these energy devices reported in recent years have been summarized.