Cobalt ferrite (CoFe₂O₄) nanoparticles were successfully synthesized by utilized sol gel method with controlled pH and temperature solution during reflux process in order to obtain monodispersed nanoparticles with high magnetic properties. The obtained cobalt ferrite particles are oval with the size vary from 100 nm to 220 nm. The Co˗O and Fe˗O bonds are formed as confirmed by FTIR measurement. The sample has high quality crystal with spinel structure as indicated by similar XRD pattern of the sample and the JCPDS (00-001-1121) data without impurity peaks. From the Vibrating Sample Magnetometer (VSM) measurement, magnetic remnant around 0.2303 emu/cc and coercive field around 2.7039 kOe are obtained.

The magnetic hysteresis curve can provide information about magnetic properties, particle size, and its distribution. For superparamagnetic materials, the characteristics of the hysteresis curve are very typical, that is, Hc is equal to zero with a certain Ms value related to particle size in the order of nanometers. Here, we report the analysis of the magnetization hysteresis curve by applying a modified Langevin equation with and without a log-normal distribution for nearly superparamagnetic Fe3O4 and Fe3O4 encapsulated by SiO2 (Fe3O4–SiO2). To study the reliability of the modified Langevin equation, we compared the particle size values obtained from fittings analysis of the modified Langevin equation with those obtained from the TEM measurement. It was found that particle size from TEM measurement for Fe3O4 and Fe3O4–SiO2 is 11 and 14 nm, respectively. These values had a very high match with the particle size obtained from fitting analysis of the modified Langevin equation with or without a log-normal distribution, which is 12.6 and 12.9 nm for Fe3O4 and 13.8 and 14.5 nm for Fe3O4–SiO2, respectively. The fitting results of the modified Langevin equation with a log-normal distribution showed a value closer to the measurement results. By using the modified Langevin equation with a log-normal distribution, it was also obtained that the probability density function for Fe3O4 was 20.69% and that for Fe3O4–SiO2 was 0.55%. It was concluded that the modified Langevin equation with and without log-normal distribution was able to be used to obtain the particle size and its distribution for nearly superparamagnetic samples.

Iron oxide of hematite (-Fe 2 O 3) has been successfully synthesized by hydrothermal method. The starting materials were Fe(NO 3) 3 .9H 2 O, 2-methoxyethanol, diethanolamine and n-hexane. The optical, morphology and crystal structure were measured by UV-VIS, TEM and XRD, respectively. From UV-VIS measurement, it was found that the band-gap of sample was 4.17 eV. The morphology of particle was plate-like form. The sample which sintered at 1100C has high quality crystal with hexagonal structure of -Fe 2 O 3 phase.

Partially Ni-substituted electron-doped superconducting cuprates of Eu_1.85Ce_0.15Cu_1-yNi_yO_4+α-δ (ECCNO) with y = 0, 0.01, 0.02 and 0.05 have been studied by muon-spin-relaxation (mSR) measurements, in order to elucidate whether or not the dynamical stripe correlations of spins and charges exist in electron-doped cuprates. It has been found that the development of the Cu-spin correlation is induced at low temperatures through the Ni substitution and that, for y = 0.02, a muon-spin precession due to a long-range magnetic order has been observed at 10 K. These results suggest a possibility that the stripe model can globally explain the high-T_c superconductivity in both hole- and electron-doped cuprates.