Hydropower dams are subjected to soft water penetration during their service lives. Concrete deterioration due to calcium leaching will decrease the durability of concrete and affect dam safety. The long-term performance of concrete dams due to calcium leaching should be evaluated and predicted accurately to complete reinforcement work in a timely manner. In this paper, a methodology that combined microscopic tests and numerical analysis to evaluate the long-term performance of dam concrete due to calcium leaching is proposed. The current state of concrete is evaluated by analyzing the components of sediments and seepage water through microscopic and spectroscopic tests, such as X-ray photoelectron spectroscopy, scanning electron microscopy, and inductively coupled plasma mass spectrometry. The long-term degradation of concrete was predicted by utilizing a multi-scale model of calcium leaching, which considered the micro-pore structure of cement hydrates flux with time. The simulated results using this calcium leaching model showed a good agreement with other experiments. Finally, a real case study including field inspection was performed and the long-term durability of dam concrete was predicted through microscopic tests and finite element analysis method. It implies that the proposed method could provide calculation and theoretical basis for the durability analysis of concrete dams due to calcium leaching.

Cementitious Capillary Crystallization Waterproofing Material (CCCW), as an efficient self-healing agent, can effectively repair damage in concrete structures, thereby extending their service life. To address the various types of damage encountered in practical engineering applications, this study investigates the impact of different mixing methods for CCCW (including internal mixing, curing, and post-crack repair) on the multi-dimensional self-healing performance of concrete. The self-healing capacity of concrete was evaluated through water pressure damage self-healing tests, freeze–thaw damage self-healing tests, mechanical load damage self-healing tests, and crack damage self-healing tests. The results show that the curing-type CCCW mixing method exhibited the best self-healing effect in repairing water pressure, freeze–thaw, and load damages, with corresponding healing rates of 88.9%, 92.7%, and 90.5%, respectively. The internally mixed CCCW method was also effective for repairing load damage in concrete, while the repair-type CCCW mixing method demonstrated the weakest repair effect on these types of damage. For concrete with induced pre-existing cracks, the internally mixed CCCW method, after 28 days of water-immersion curing, exhibited a significantly higher crack self-healing ability, with a self-healing ratio of 333.8%. Optical microscopy observations revealed that the crack surfaces were almost fully sealed, with a substantial deposition of white crystalline material at the crack sites. Further analysis using scanning electron microscopy (SEM) and X-ray Diffraction (XRD) provided insights into the surface morphology and phase characteristics of the self-healed cracks, indicating that calcium carbonate (CaCO₃) and calcium silicate hydrate (C-S-H) were the main products responsible for crack healing.

Civil air defence works are underground buildings with specific functions, which should not only meet various demands in wartime but also be compatible with the development of urban economy. These buildings usually act as shopping malls, restaurants, exhibition halls, stadiums and the like in peacetime. Any ill-considered fire protection design of such works is extremely likely to cause great casualties and property losses in case of fire. The fire protection design of buildings in the Code for Fire Protection Design of Civil Air Defence Works has been perused and some thoughts have been demonstrated in combination with the current situations.