Currently, low heat Portland (LHP) cement is widely used in mass concrete structures. The magnesia expansion agent (MgO) can be adopted to reduce the shrinkage of conventional Portland cement-based materials, but very few studies can be found that investigate the influence of MgO on the properties of LHP cement-based materials. In this study, the influences of two types of MgO on the hydration, as well as the shrinkage behavior of LHP cement-based materials, were studied via pore structural and fractal analysis. The results indicate: (1) The addition of reactive MgO (with a reactivity of 50 s and shortened as M50 thereafter) not only extends the induction stage of LHP cement by about 1–2 h, but also slightly increases the hydration heat. In contrast, the addition of weak reactive MgO (with a reactivity of 300 s and shortened as M300 thereafter) could not prolong the induction stage of LHP cement. (2) The addition of 4 wt.%–8 wt.% MgO (by weight of binder) lowers the mechanical property of LHP concrete. Higher dosages of MgO and stronger reactivity lead to a larger reduction in mechanical properties at all of the hydration times studied. M300 favors the strength improvement of LHP concrete at later ages. (3) M50 effectively compensates the shrinkage of LHP concrete at a much earlier time than M300, whereas M300 compensates the long-term shrinkage more effectively than M50. Thus, M300 with an optimal dosage of 8 wt.% is suggested to be applied in mass LHP concrete structures. (4) The addition of M50 obviously refines the pore structures of LHP concrete at 7 days, whereas M300 starts to refine the pore structure at around 60 days. At 360 days, the concretes containing M300 exhibits much finer pore structures than those containing M50. (5) Fractal dimension is closely correlated with the pore structure of LHP concrete. Both pore structure and fractal dimension exhibit weak (or no) correlations with shrinkage of LHP concrete.

A partial-depth, diamond-shaped, ultra-high performance concrete (UHPC) connection with embedded transverse reinforcement between adjacent precast prestressed concrete voided beams (APPCVBs) has been developed by the Federal Highway Administration (FHWA) to overcome the disadvantages of longitudinal cracks within the connections. In this study, the shear behavior of 14 spliced panel specimens with the FHWA developed UHPC connection will be experimentally investigated. One monolithic specimen will be tested as a reference. The test parameters include surface preparation, the compressive strength of the filling concrete, lateral reinforcement details, and the lateral reinforcement diameter. The shear behavior will be evaluated from cracking patterns, failure modes, load–deflection responses, and ultimate load capacity. Formulas will be derived based on the elastic beam theory coupled with the dowel effect of transverse reinforcement. The derived formulas could generally predict the shear strength of the spliced panel specimens with the FHWA developed UHPC connection.

In recent years, with the acceleration of urbanization and the continuous expansion of construction at all scales, the safety, durability, and sustainability of building structures have come to face multiple challenges

The corrosion of alkaline concrete materials exposed to a sulfuric acid environment is becoming more and more prevalent, and its damage assessment is becoming more and more imperative. This study aims to describe the corroded surfaces of concrete with different strength grades (C30, C50, C80) in sulfuric acid environments in terms of their three-dimensional fractal dimension. Three kinds of concrete with varying strength grades, namely C30, C50, and C80, were immersed in a sulfuric acid solution with pH ≈ 0.85 for four distinct corrosion durations, specifically 0, 28, 56, and 165 days, in accelerated corrosion tests. The 3D laser scanning technique was utilized to capture the 3D coordinates of the surface points of the concrete cylinder before and after corrosion. The fractal dimension of concrete’s uneven surface before and after corrosion was computed via the cube covering method, and the mass loss of the concrete specimen was also obtained. The outcomes demonstrate that the three-dimensional fractal dimension provides a new method for characterizing the degree of corrosion deterioration of concrete samples affected by sulfuric acid via laser scanning technology. From the perspective of the appearance, mass loss, and fractal dimension of a rough surface in the sulfuric acid environment at a pH level of approximately 0.85, the degree of the corrosion deterioration of concrete is ranked from high to low as C80 > C50 > C30. These fractal dimensions of the concrete’s corroded surfaces with various strength grades increase rapidly in the initial period. However, as the corrosion time progresses, the growth rate of the corroded surface fractal dimension gradually decelerates and tends towards stability, which accords with the law of exponential function. The widespread belief is that the higher the strength grade of concrete, the better its durability; however, this pattern varies in sulfuric acid corrosive environments. Therefore, based on this research, it is recommended that in extremely acidic environments (i.e., very low pH), more attention should be paid to high-strength grades of concrete.

Prefabricated Ultra-High-Performance Concrete (UHPC) and cast-in-place Normal Concrete (NC) composite members are increasingly used in bridge engineering because they combine high performance with cost-effectiveness. The bond at the UHPC-NC interface is critical as it directly impacts the composite structure’s safety. This study employed 3D laser scanning acquired the UHPC substrate geometry, utilized fractal dimension analysis to quantify the interface roughness, and adopted the slant shear test to evaluate the effects of retarder application mass and hydration delay duration on roughness and bond strength. The research results indicate that the failure modes of UHPC-NC specimens can be categorized into interface shear failure and NC splitting tensile failure. With the extension of hydration delay duration, both the interface roughness and bond strength show a decreasing trend. The influence of retarder dosage on interface roughness and bond strength exhibits a threshold effect. This study also confirms the effectiveness of fractal dimension as a quantitative tool for characterizing the macroscopic roughness features of the bonding interface. The findings of this paper provide a solid theoretical basis and quantitative support for optimizing key process parameters such as retarder dosage and precisely controlling hydration delay duration, offering significant engineering guidance for enhancing the interface bonding performance of UHPC-NC composite structures.