Due to their biodegradability and biocompatibility, chitosan-based hydrogels have great potential in regenerative medicine, with applications such as bacteriostasis, hemostasis, and wound healing. However, toxicity and high cost are problems that must be solved for chitosan-based hydrogel crosslinking agents such as formaldehyde, glutaraldehyde, and genipin. Therefore, we developed a biocompatible yet cost-effective chitosan-based hydrogel system as a candidate biomaterial to prevent infection during wound healing. The hydrogel was fabricated by crosslinking chitosan with dialdehyde chitosan (CTS–CHO) via dynamic Schiff-base reactions, resulting in a self-healable and injectable system. The rheological properties, degradation profile, and self-healable properties of the chitosan-based hydrogel were evaluated. The excellent antibacterial activity of the hydrogel was validated by a spread plate experiment. The use of Live/Dead assay on HEK 293 cells showed that the hydrogel exhibited excellent biocompatibility. The results demonstrate that the newly designed chitosan-based hydrogel is an excellent antibacterial wound dressing candidate with good biocompatibility.

To explore the potential applicability of chitosan (CTS), we prepared aldehyde chitosan (CTS-CHO) with chitosan and sodium periodate via oxidation reaction and then a chitosan-based hydrophilic and antibacterial coating on the surface of poly (lactic acid) (PLA) film was developed and characterized. The oxidation degree was determined by Elemental analyser to be 12.53%, and a Fourier transform infrared spectroscopy was used to characterize the structure of CTS-CHO. It was evident that CTS-CHO is a biocompatible coating biomaterial with more than 80% cell viability obtained through the Live/Dead staining assay and the alamarBlue assay. The hydrophilic and antibacterial CTS-CHO coating on the PLA surface was prepared by ultrasonic atomization assisted LbL assembly technique due to Schiff’s base reaction within and between layers. The CTS-CHO coating had better hydrophilicity and transparency, a more definite industrialization potential, and higher antibacterial activity at experimental concentrations than the CTS coating. All of the results demonstrated that the ultrasonic atomization-assisted LbL assembly CTS-CHO coating is a promising alternative for improving hydrophilicity and antibacterial activity on the PLA surface. The functional groups of CTS-CHO could react with active components with amino groups via dynamic Schiff’s base reaction and provide the opportunity to create a drug releasing surface for biomedical applications.