This research focuses on the plant-mediated green synthesis process to produce gold nanoparticles (Au NPs) using upland cress (Barbarea verna), as various biomolecules within the upland cress act as both reducing and capping agents. The synthesized gold nanoparticles were thoroughly characterized using UV-vis spectroscopy, surface charge (zeta potential) analysis, scanning electron microscopy-energy-dispersive X-ray spectroscopy (SEM-EDX), atomic force microscopy (AFM), attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR), and X-ray diffraction (XRD). The results indicated the synthesized Au NPs are spherical and well-dispersed with an average diameter ~11 nm and a characteristic absorbance peak at ~529 nm. EDX results showed an 11.13% gold content. Colloidal Au NP stability was confirmed with a zeta potential (ζ) value of −36.8 mV. X-ray diffraction analysis verified the production of crystalline face-centered cubic gold. Moreover, the antimicrobial activity of the Au NPs was evaluated using Gram-negative Escherichiacoli and Gram-positive Bacillus megaterium. Results demonstrated concentration-dependent antimicrobial properties. Lastly, applications of the Au NPs in catalysis and biomedicine were evaluated. The catalytic activity of Au NPs was demonstrated through the conversion of 4-nitrophenol to 4-aminophenol which followed first-order kinetics. Cellular uptake and cytotoxicity were evaluated using both BMSCs (stem) and HeLa (cancer) cells and the results were cell type dependent. The synthesized Au NPs show great potential for various applications such as catalysis, pharmaceutics, and biomedicine.

This article reports that it is possible to make multifunctional sensing devices with ZnO infiltrated polymers while the sensing interactions could occur throughout the polymer. As such, we find that infiltrated devices with SU-8 polymer can result in highly sensitive UV sensors. Mesh dielectric core devices were found to make sensitive gas sensors with a better than 5 ppm sensitivity for formaldehyde and NO₂. A new type of p-n junction device is further demonstrated that is sensitive to UV illumination, thus making it an enhanced UV sensor. Sensing devices relying on volume interactions, such as light absorption, can significantly benefit from the infiltrated polymer. In contrast, devices that rely on surface interactions, such as gas sensors, do not gain performance in any significant way with or without the infiltrated polymer.

The goal of this research was to develop a novel oxygen therapeutic made from a pectin-based hydrogel microcapsule carrier mimicking red blood cells. The study focused on three main criteria for developing the oxygen therapeutic to mimic red blood cells: size (5–10 μm), morphology (biconcave shape), and functionality (encapsulation of oxygen carriers; e.g., hemoglobin (Hb)). The hydrogel carriers were generated via the electrospraying of the pectin-based solution into an oligochitosan crosslinking solution using an electrospinning setup. The pectin-based solution was investigated first to develop the simplest possible formulation for electrospray. Then, Design-Expert^® software was used to optimize the production process of the hydrogel microcapsules. The optimal parameters were obtained through the analysis of a total of 17 trials and the microcapsule with the desired morphology and size was successfully prepared under the optimized condition. Fourier transform infrared spectroscopy (FTIR) was used to analyze the chemistry of the microcapsules. Moreover, the encapsulation of Hb into the microcapsule did not adversely affect the microcapsule preparation process, and the encapsulation efficiency was high (99.99%). The produced hydrogel microcapsule system shows great promise for creating a novel oxygen therapeutic.

An exfoliated MoS₂ encapsulated into metal-organic frameworks (MOFs) was fabricated as a promising noble-metal-free photocatalyst for hydrogen production under visible light irradiation. The as-synthesized samples were examined by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), and Brunauer–Emmett–Teller (BET) surface analysis. It is well known that bulk MoS₂ is unsuitable for photocatalysis due to its inadequate reduction and oxidation capabilities. However, exfoliated MoS₂ exhibits a direct band gap of 2.8 eV due to quantum confinement, which enables it to possess suitable band positions and retain a good visible-light absorption ability. As a result, it is considered to be an encouraging candidate for photocatalytic applications. Encapsulating exfoliated MoS₂ into MOF demonstrates an improved visible light absorption ability compared to pure MOF, and the highest hydrogen production rate that the encapsulated exfoliated MoS₂ could reach was 68.4 μmol h^-1g^-1, which was much higher than that of pure MOF. With a suitable band structure and improved light-harvesting ability, exfoliated MoS₂@MOF could be a potential photocatalyst for hydrogen production.

The development of vascularized tissue is a substantial challenge within the field of tissue engineering and regenerative medicine. Studies have shown that positively-charged microspheres exhibit dual-functions: (1) facilitation of vascularization and (2) controlled release of bioactive compounds. In this study, gelatin-coated microspheres were produced and processed with either EDC or transglutaminase, two crosslinkers. The results indicated that the processing stages did not significantly impact the size of the microspheres. EDC and transglutaminase had different effects on surface morphology and microsphere stability in a simulated colonic environment. Incorporation of EGM and TGM into bioink did not negatively impact bioprintability (as indicated by density and kinematic viscosity), and the microspheres had a uniform distribution within the scaffold. These microspheres show great potential for tissue engineering applications.

A major challenge in tissue engineering is the formation of vasculature in tissue and organs. Recent studies have shown that positively charged microspheres promote vascularization, while also supporting the controlled release of bioactive molecules. This study investigated the development of gelatin-coated pectin microspheres for incorporation into a novel bioink. Electrospray was used to produce the microspheres. The process was optimized using Design-Expert^® software. Microspheres underwent gelatin coating and EDC catalysis modifications. The results showed that the concentration of pectin solution impacted roundness and uniformity primarily, while flow rate affected size most significantly. The optimal gelatin concentration for microsphere coating was determined to be 0.75%, and gelatin coating led to a positively charged surface. When incorporated into bioink, the microspheres did not significantly alter viscosity, and they distributed evenly in bioink. These microspheres show great promise for incorporation into bioink for tissue engineering applications.