Nonlinear finite element (FE) analysis of reinforced concrete (RC) structures is characterized by numerous modeling options and input parameters. To accurately model the nonlinear RC behavior involving concrete cracking in tension and crushing in compression, practitioners make different choices regarding the critical modeling issues, e.g., defining the concrete constitutive relations, assigning the bond between the concrete and the steel reinforcement, and solving problems related to convergence difficulties and mesh sensitivities. Thus, it is imperative to review the common modeling choices critically and develop a robust modeling strategy with consistency, reliability, and comparability. This paper proposes a modeling strategy and practical recommendations for the nonlinear FE analysis of RC structures based on parametric studies of critical modeling choices. The proposed modeling strategy aims at providing reliable predictions of flexural responses of RC members with a focus on concrete cracking behavior and crushing failure, which serve as the foundation for more complex modeling cases, e.g., RC beams bonded with fiber reinforced polymer (FRP) laminates. Additionally, herein, the implementation procedure for the proposed modeling strategy is comprehensively described with a focus on the critical modeling issues for RC structures. The proposed strategy is demonstrated through FE analyses of RC beams tested in four-point bending—one RC beam as reference and one beam externally bonded with a carbon-FRP (CFRP) laminate in its soffit. The simulated results agree well with experimental measurements regarding load-deformation relationship, cracking, flexural failure due to concrete crushing, and CFRP debonding initiated by intermediate cracks. The modeling strategy and recommendations presented herein are applicable to the nonlinear FE analysis of RC structures in general.

Soil–steel composite bridges (SSCB) have become increasingly popular for short-span bridges as an alternative to concrete slab bridges mainly due to their low initial cost, rapid manufacture, simplified construction, and geometrical adaptability. SSCBs have a variety of applications and can be used over waterways or roadways. While conventional bridges tend to lose their load-carrying capacity due to degradation, SSCBs gain strength because of backfill soil consolidation. However, the load carrying capacity and integrity of such structures highly depends on the condition and load-carrying capacity of the steel arch element. A major drawback of SSCBs, especially those located on waterways or with poor drainage, is corrosion and subsequent loss of cross-sectional capacity. Unfortunately, the inspection of such bridges is not straightforward and any damage/collapse will be very costly to repair/replace. Fiber reinforced polymer (FRP) composites offer an attractive alternative to replace the steel in these types of bridges. FRP composites have significantly improved durability characteristics compared to steel, which will reduce maintenance costs and improve life-cycle costs (LLCs). This paper presents a new concept to use glass FRP as a construction material to construct soil–FRP composite bridges (SFCB). Various aspects of design and manufacturing are presented along with results and conclusions from a case study involving alternative bridge designs in steel and FRP composites.