The extensive usage of concrete and ordinary Portland cement has generated 5~8% of annual global CO₂ emissions, causing serious environmental problems. To reduce such environmental impact, researchers have made significant efforts to develop alternative materials that may partially or entirely replace the ordinary Portland cement, such as limestone calcined clay cement (LC3). LC3 has not been commonly adopted in reality because of uncertain setting times during the transportation and construction processes. Comprehensive investigation and understanding of the setting times of LC3 has great significance to industrial upgrading. As a result, this study is committed to comprehensively reviewing the hydration process and the setting time of LC3 materials.

Concrete is known as the most globally used construction material, but it releases a huge amount of greenhouse gases due to cement production. Recently, Supplementary Cementitious Materials (SCMs) such as fly ash and Ground Granulated Blast Furnace Slag (GGBFS) have been widely used in concrete to reduce the cement content. However, SCMs can alter the mechanical properties and time-dependent behaviors of concrete and the early age mechanical properties of concrete significantly affect the concrete cracking in the engineering field. Therefore, evaluation of the development of the mechanical properties of SCMs-based concrete is vital. In this paper, the time development of mechanical properties of concrete mixes with various fly ash and GGBFS was experimentally investigated. Four different cement replacement levels including 0%, 20%, 30%, and 40% by fly ash and GGBFS as well as ternary binders were considered. Compressive strength, splitting tensile strength, flexural strength, and elastic modulus of concrete were measured until 28 days. Three additional concrete mixes with ternary binders were also cast to investigate the early-age autogenous shrinkage development until 28 days. In addition, prediction models in existing standards were used and compared to experimental results. The comparison results showed that the prediction models overestimated the compressive strength but underestimated the splitting tensile strength development and autogenous shrinkage. As a result, a model capturing the effect of fly ash and GGBFS on the development of compressive and splitting tensile strength is proposed to improve the prediction accuracy for current standards and empirical models.

Supplementary cementitious materials (SCMs) are eco-friendly cementitious materials that can partially replace ordinary Portland cement (OPC). The occurrence of early-age cracking in OPC-SCM blended cement is a significant factor impacting the mechanical properties and durability of the concrete. This article presents a comprehensive review of the existing research on cracking in OPC-SCM concrete mix at early ages. To assess the effects of SCMs on the early-age cracking of concrete, the properties of blended cement-based concrete, in terms of its viscoelastic behavior, evolution of mechanical performance, and factors that affect the risk of cracking in concrete at early ages, are reviewed. The use of SCMs in OPC-SCM concrete mix can be an effective method for mitigating early-age cracking while improving the properties and durability of concrete structures. Previous research showed that the shrinkage and creep of OPC-SCM concrete mix are lower than those of conventional concrete. Moreover, the lower cement content of OPC-SCM concrete mix resulted in a better resistance to thermal cracking. Proper selection, proportioning, and implementation of SCMs in concrete can help to optimize the performance and reduce the environmental impact of OPC-SCM concrete mix.