This review covers the state-of-the-art in the production of lignin-based carbon adsorbents for CO ₂ capture, discussing lignin chemistry and properties, traditional synthesis approaches to emerging methods, and fundamentals for rational design.

Ecologically friendly wood electronics will help alleviating the shortcomings of state-of-art cellulose-based “green electronics”. Here we introduce iron-catalyzed laser-induced graphitization (IC-LIG) as an innovative approach for engraving large-scale electrically conductive structures on wood with very high quality and efficiency, overcoming the limitations of conventional LIG including high ablation, thermal damages, need for multiple lasing steps, use of fire retardants and inert atmospheres. An aqueous bio-based coating, inspired by historical iron-gall ink, protects wood from laser ablation and thermal damage while promoting efficient graphitization and smoothening substrate irregularities. Large-scale (100 cm²), highly conductive (≥2500 S m⁻¹) and homogeneous surface areas are engraved single-step in ambient atmosphere with a conventional CO₂ laser, even on very thin (∼450 µm) wood veneers. We demonstrate the validity of our approach by turning wood into highly durable strain sensors, flexible electrodes, capacitive touch panels and an electroluminescent LIG-based device.

Mechanically robust and renewable Janus wood membranes with capability for autonomous water transport show excellent fog-capturing efficiency.

In this work, a different polymer chain structure was synthesized to study π-π interactions between polymer and reduced graphene oxide (RGO). Polymers with different chain structures were obtained from free radical copolymerization of styrene with 4-cyanostyrene (containing substituted phenyl rings) and 2-vinylnaphthalene (containing naphthalene rings). In this work, the polystyrene, poly(styrene-co-4-cyanostyrene) and poly(styrene-co-2-vinylnaphthalene) were named as PS, PSCN and PSNP, respectively. RGO was prepared through modified Hummers’ method and further thermal reduction, and nanocomposites were prepared by solution blending. Thus, different π-π interactions were formed between polymers and RGO. Raman and thermal gravimetric analysis (TGA) were used to characterize the interfacial interaction, showing that the trend of the interfacial interaction should be in the order of RGO/PSCN, RGO/PS, and RGO/PSNP. The differential scanning calorimetry (DSC) measurement showed that, compared with polymer matrix, the glass transition temperature (T_g) of RGO/PS, RGO/PSCN and RGO/PSNP nanocomposites with the addition of 4.0 wt% RGO are increased by 14.3 °C, 25.2 °C and 4.4 °C, respectively. Compared with π-π interaction only formed through aromatic rings, substituent groups changed the densities of electron clouds on the phenyl rings. This change resulted in the formation of donor-acceptor interaction and reinforcement of the π-π interaction at the interface, which leads to increased value of T_g. This comparative study can be useful for selecting appropriate interaction groups, as well as suitable monomers, to prepare high performance nanocomposites.