A high-efficiency inverted-type CH₃NH₃PbI₃ (MAPbI₃) solar cell was fabricated by using a ultrathin poly[3-(4-carboxybutyl)thiophene-2,5-diyl]-Na (P3CT-Na) film as the hole transport layer. The averaged power conversion efficiency (PCE) can be largely increased from 11.72 to 18.92% with a double-filtering process of the P3CT-Na solution mainly due to the increase in short-circuit current density (J_SC) from 19.43 to 23.88 mA/cm², which means that the molecular packing structure of P3CT-Na thin film can influence the formation of the MAPbI₃ thin film and the contact quality at the MAPbI₃/P3CT-Na interface. Zeta potentials, atomic-force microscopic images, absorbance spectra, photoluminescence spectra, X-ray diffraction patterns, and Raman scattering spectra are used to understand the improvement in the J_SC. Besides, the light intensity-dependent and wavelength-dependent photovoltaic performance of the MAPbI₃ solar cells shows that the P3CT-Na thin film is not only used as the hole transport layer but also plays an important role during the formation of a high-quality MAPbI₃ thin film. It is noted that the PCE values of the best P3CT-Na based MAPbI₃ solar cell are higher than 30% in the yellow-to-near infrared wavelength range under low light intensities. On the other hand, it is predicted that the double-filtering method can be readily used to increase the PCE of polymer based solar cells.

A series of novel double-anchoring dyes for phenoxazine-based organic dyes with two 2-cyanoacetic acid acceptors/anchors, and the inclusion of a 2-ethylhexyl chain at the nitrogen atom of the phenoxazine that is connected with furan, thiophene, and 3-hexylthiophene as a linker, are used as sensitizers for dye-sensitized solar cells. The double-anchoring dye exhibits strong electronic coupling with TiO₂, provided that there is an efficient charge injection rate. The result showed that the power conversion efficiency of DP-2 with thiophene linker-based cell reached 3.80% higher than that of DP-1 with furan linker (η = 1.53%) under standard illumination. The photovoltaic properties are further tuned by co-adsorption strategy, which improved power conversion efficiencies slightly. Further molecular theoretical computation and electrochemical impedance spectroscopy analysis of the dyes provide further insight into the molecular geometry and the impact of the different π-conjugated spacers on the photophysical and photovoltaic performance.