We here demonstrate a facile one-step synthesis of RGO–Ni hybrid materials, where Ni²⁺ ions and GO are simultaneously reduced by γ-irradiation. RGO–Ni, with Ni nanoparticles well dispersed on the RGO surface, shows a more enhanced EM absorption ability than the individuals.

Microwave absorbers that are lightweight and have good stability and high efficiency have attracted much attention for their applications in many contemporary fields. In this work, a 3D porous (Ni@NO-C)_n/NO-C composite absorber was prepared using a wet chemistry method with Ni chains and melamine as precursors, in which NO-C (N,O-doped carbon)-encapsulated Ni particles are homogenously dispersed in the 3D porous networks of NO-C in the form of (Ni@NO-C)_n chains. The special microstructure of the as-prepared material is proven to be beneficial for the improvement of its microwave absorption performance. The as-synthesized (Ni@NO-C)_n/NO-C composite absorber exhibited an effective absorption bandwidth of 4.1 GHz and an extremely large reflection loss of −72.3 dB. The excellent microwave-absorbing performances can be ascribed to the cooperative consequences of dielectric loss and magnetic loss, along with the balance between attenuation capability and impedance matching.

A series of Tantalum Nitride (TaN) films under a reactive direct current magnetron sputtering method with a controlled total gas flow rate were prepared on aluminum oxide substrates. To find the nitrogen flow rate, which produced the minimum sheet resistance, TaN films deposited under a nitrogen gas flow ratio of 2.5%, 5%, 10%, 15%, 20%, 25% were characterized in terms of their structural and electrical properties. The optimum total gas flow rate was 60 sccm, revealing the lowest deviation of sheet resistance. Next, the durability and reliability at high temperatures, after heating and cooling cycles and exposure to the induced current, were tested. When the nitrogen flow ratio reaches 2.5%, it gets the maximum for the adhesion force, roughness, and deposition rate of the TaN film, and maximum values are 75.4 N, 1.1 nm, and 3.67 nm/min, respectively, and the sheet resistance of the TaN film reaches a minimum of 20.32 Ω/sq. The degradation behaviors and failure of TaN films were investigated by measuring the sheet resistance variation. To further explain the degradation of TaN films, additional analysis of their crystallinity was conducted. The results showed that TaN-based thin film resistors have high durability and reliability, and are suitable for embedded passive resistors.

Zinc ions, as essential trace elements in the human body, play a crucial role in promoting wound healing. They have significant applications in the medical field. In this paper, chitosan (CS)/polyvinyl alcohol (PVA)/zinc gluconate hydrogel was synthesized via gamma ray irradiation cross-linking. The hydrogel exhibited excellent antibacterial properties, and could continuously release zinc ions. Antibacterial assays demonstrated that the combination of CS and zinc ions improved the antibacterial properties of hydrogel. The inhibition zones against both Staphylococcus aureus and Escherichia coli exceed 12 mm. The cell viability can reach 108.25%. The prepared hydrogel could continuously release zinc ions over a period of 70 h. The pore and chemical structure were, respectively, performed using scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FT-IR). And its comprehensive properties, such as gel content, water evaporation ratio and swelling behavior were investigated. The hydrogels showed potential application value in the hydrogel dressing for zinc ion delivery.