Reports of the influence of surface roughness on the adhesion and tribological performance of contemporary nitride coatings with different layer designs are still scarce in the literature. Therefore, in this study, we evaluated the behavior of a single-layer TiAlN, a bilayer TiAlN/CN_x, and a nanolayer AlTiN/TiN coating. Coatings were deposited in an industrial magnetron sputtering unit on the substrates of EN 100Cr6 steel, prepared to four degrees of surface roughness (Sa = 10–550 nm). The coatings’ adhesion was determined by scratch tests performed perpendicular and parallel to the machining marks. Dry reciprocating sliding tests in air were employed to evaluate the coatings’ tribological behavior against an Al₂O₃ ball. Before and after the tests, coating properties were characterized by 3D profilometry, confocal microscopy, and energy dispersive spectroscopy. Deposition of all coatings significantly altered the surface topography and increased the roughness of the samples. No general rule could be established for the effect of surface roughness on tribological behavior and adhesion of different hard coatings. For very fine surface finishes the adhesion and tribological performance of TiAlN and TiAlN/CN_x coatings was independent of the surface roughness. For the roughest surfaces, a decrease in adhesion and an increase in the wear rate were observed. The AlTiN/TiN coating exhibited the largest sensitivity of adhesion to roughness and scratching direction. The coefficient of friction and wear rate increased when AlTiN/TiN roughness exceeded Sa ≈ 100 nm.

In this study, we used the depth-sensing indentation technique to determine the cracking resistance of different PVD hard coatings deposited on tool steel substrates. By comparison, with the load–displacement curves, measured at the sites of carbide inclusion and a tempered martensite matrix in the D2 tool steel substrate surface, we observed different fracture mechanisms on TiAlN hard coating prepared by sputtering. Additional information about the deformation and fracture phenomena was obtained from the SEM images of FIB cross-sections of both types of indents. We found that the main deformation mechanism in the coating is the shear sliding along the columnar boundaries, which causes the formation of steps on the substrate surface under individual columns. Using nanoindentation test, we also analyzed the cracking resistance of a set of nl-(Cr,Al)N nanolayer coatings with different Cr/Al atomic ratios, which were sputter deposited in a single batch. From the indentation curves, we determined the loads (F_c) at which the first pop-in appears and compared them with the plasticity index H³/E². A good correlation of both parameters was found. We also compared the indentation curves of the TiAlN coating, which were prepared by cathodic arc evaporation using 1-fold, 2-fold and 3-fold rotation of the substrates. Additionally, on the same set of samples, the fracture toughness measurements were performed by micro-cantilever deflection test. The impact of growth defects on the cracking resistance of the hard coatings was also confirmed.