This article explores the influence of transverse reinforcement (spiral) and high-strength longitudinal reinforcements on the physical-mechanical properties of centrifuged annular cross-section elements of concrete. The test results of almost 200 reinforced, and over 100 control elements are summarizing in this article. The longitudinal reinforcement ratio of samples produced in the laboratory and factory varied from 1.0% to 6.0%; the transverse reinforcement ratio varied from 0.25% to 1.25%; the pitch of spirals varied from 100 mm to 40 mm and the concrete strength varied from 25 MPa to 60 MPa. Experimental relationships of coefficients for concrete strength, moduli of elasticity and limits of the longitudinal strain of centrifuged concrete in reinforced concrete structures in short-term concentrically compression were proposed.

The current research paper is focused on the experimental investigation of features of chemical admixtures (superplasticizers C-3, ‘Dofen’ and formaldehyde resin ACF-3M) utilizing in reinforced spun concrete structures. For the sake of comparison, the results of studying the effects of chemical admixtures on physical and mechanical properties on vibrated and spun concrete are provided. As a separate part of spun concrete products, the supporting poles of overhead power lines are introduced. The results obtained indicate, that the positive effect of chemical admixtures for spun and vibrated concrete is most pronounced at an early age of concrete. The effective amount of chemical admixtures for spun concrete is 0.15% of cement mass when formaldehyde resin ACF-3M and 1% of cement mass when superplasticizers C-3 and ‘Dofen’ are used. Moreover, the brief review about the reinforced spun concrete members is provided.

The present paper focused on the investigation of the effectiveness of using various chemical admixtures and their effect on the strength and deformability of the reinforced spun concrete members—the supporting poles of the overhead power transmission lines—under the unfavorable long-term combined action of the aggressive salt-saturated groundwater and the temperature changes. According to the long-term experimental program, 96 prismatic spun concrete specimens were subjected to multi-cycle (25-50-75 cycles) processing under the combined aggressive environmental conditions. It has been found that chemical admixtures which decrease the initial water-cement ratio produce a considerable positive effect on the mechanical properties of spun concrete used in hot and arid climates and exposed to physical salt attack (PSA). Superplasticizers decrease the initial water-cement ratio the most, and, due to a unique concrete compaction method used, they produce the most homogeneous and dense concrete structure. They can be recommended as most effective in increasing the durability of spun concrete used under the above-mentioned aggressive environmental conditions.

Cement-grouted injections are increasingly employed as a countermeasure material against liquefaction in active seismic areas; however, there is no methodology to thoroughly and directly evaluate the liquefaction potential of saturated sand materials reinforced by the cement grout-injected micropiles. To this end, first, a series of 1 g shaking table model tests are conducted. Time histories of pore water pressures, excess pore water pressure ratios (r_u), and the number of required cycles (N_peak) to liquefy the soil are obtained and modified lower and upper boundaries are suggested for the potential of liquefaction of both pure and grout-reinforced sand. Next, adopting genetic programming and the least square method in the framework of the evolutionary polynomial regression technique, high-accuracy predictive equations are developed for the estimation of r_umax. Based on the results of a three-dimensional, graphical, multiple-variable parametric (MVP) analysis, and introducing the concept of the critical, boundary inclination angle, the inclination of micropiles is shown to be more effective in view of liquefaction resistivity for loose sands. Due to a lower critical boundary inclination angle, the applicability range for inclining micropiles is narrower for the medium-dense sands. MVP analyses show that the effects of a decreasing spacing ratio on decreasing r_umax are amplified while micropiles are inclined.