In this work, photocatalytic performance is divulged in the ternary CuO-Ag-ZnO nanowire synthesized via a two-step approach. The decoration of Ag and CuO nanostructures onto the surface of ZnO nanowires was simply carried out by using the plasma electrolytic oxidation method in a short time. The structure, size, morphology, and optical properties of as-prepared samples were characterized by X-ray diffraction, field-emission scanning electron microscopy, and spectrophotometry measurements. The diameters of Ag nanoparticles and ZnO nanoflowers are in the range of 5–20 nm and 20–60 nm, respectively. Within the first 15 min, methyl orange was decolorized 96.3 and 82.8% in the CuO-Ag-ZnO and Ag-ZnO, respectively, and there is only about 46.7% of that decomposed in pure ZnO. The CuO-Ag-ZnO shows a higher rate constant k = 0.2007 min⁻¹ and a lower half-life time t = 6.1 min compared to Ag-ZnO and bare ZnO nanowires. The photo-reusability of the ternary nanostructures was estimated to be much outweighed compared to ZnO nanowires. Interestingly, the synergic incorporation between noble metal–semiconductor or semiconductor–semiconductor in the interfaces of Ag-CuO, Ag-ZnO, and CuO-ZnO expands the visible light absorption range and eliminates the photogenerated electron–hole recombination, resulting in a superior visible-light-driven photocatalyst.

We have designed an excellent visible-light-driven and high-performance photocatalyst with a Ag-Cu₂O-ZnO nanowire heterostructure in our work by combining the hydrothermal approach with plasma–liquid technology. The structural and morphological characteristics and optical properties of the samples were evaluated using X-ray diffraction, field-emission scanning electron microscopy, and spectrophotometry, respectively. The results show that the Ag nanoparticles are mainly positioned on the Cu₂O nanoclusters compared with the ZnO nanowire surface, forming broccoli-like Ag-Cu₂O nanoclusters during the Ar gas plasma treatment process in an aqueous solution. The diameter of the Ag/Cu₂O nanoclusters ranges from 150 to 180 nm. The Ag-Cu₂O-ZnO nanowires exhibited improved photocatalytic performance, decomposing approximately 98% methyl orange dye in 30 min. This is a consequence of the synergistic interactions between the p-n heterojunction formed at the Cu₂O-ZnO interfaces and the localized surface plasmon resonance (LSPR) effect of the Ag nanoparticles, which broaden the visible light absorption range and effectively separate the photogenerated charge carriers.