The reaction of citric acid with wood veneers was studied by Cross Polarization Magic Angle Spinning Nuclear Magnetic Resonance (CP MAS ¹³C NMR) and matrix assisted laser desorption ionization time of flight (MALDI ToF) mass spectrometry. The analysis showed that reactions of citric acid occurred with both lignin and carbohydrate constituents of wood. The reactions occurring are esterifications between the carboxylic acid functions of citric acid and the numerous aromatic and aliphatic hydroxyl groups of the main wood constituents. Reaction of citric acid with glucose as a simple model compound of carbohydrates hydroxyl groups also yielded reactions leading to linear and branched oligomers by esterification. The result indicate that the reactions of esterification are accompanied in parallel by some internal rearrangements of lignin. The applied results on bonding wide flat wood surfaces such as veneers to obtain LVL panels yielded excellent strength results even if the conditions of pressing were more drastic than what is usual for this application. The applied bonding results have shown that citric acid has great potential to be used as a bio-binder for wood veneers.

Mostly biosourced non-isocyanate polyurethanes (NIPU) were prepared from mono- and disaccharides, namely glucose and sucrose, reacted with dimethyl carbonate and hexamethylene diamine. The main aim of this research was to show that NIPU can be prepared from mono- and disaccharides, this just being an initial exploratory work and its sole main aim. The oligomers obtained were detected by MALDI-ToF, CP-MAS ¹³C NMR, and FTIR spectrometries. The glucose-derived NIPU were shown to harden at a markedly lower temperature than the sucrose-derived ones and to be easier to handle and spread. The NIPU obtained were applied as wood and steel surface coatings and tested by the sessile drop test (on wood) and cross-cut test (on steel) with encouraging results. The glucose NIPU gave good surface coating results already at 103 °C, while the sucrose NIPU yielded good results only at a markedly higher temperature of hardening. The NIPU saccharide resins were also tested as thermosetting wood joint adhesives with the glucose NIPU yielding very encouraging results.

A partially biobased self-blowing and self-hardening polyurethane foam from glucose-based non-isocyanate polyurethanes (g-NIPU) was prepared by reaction of glucose with dimethyl carbonate and hexamethylene diamine. However, these foam types generally require a high foaming temperature. In this paper, a self-blowing foam based on g-NIPU was prepared at room temperature by using maleic acid as an initiator and glutaraldehyde as a crosslinker. Water absorption, compression resistance, and fire resistance were tested. Scanning electron microscopy (SEM) was used to observe the foam cells structure. Middle infrared (ATR FT-MIR) and Matrix Assisted Laser Desorption Ionization Time-of-Flight (MALDI-TOF) mass spectrometry were used to help to analyze the reactions during the foaming process. The results obtained showed that self- blowing rigid foams have good compression, this being directly proportional to the foam density. Increasing the amount of glutaraldehyde or reducing maleic acid thickens the cell walls and increases the density of the foams. MALDI-TOF analysis showed that g-NIPU reacts with both maleic acid and glutaraldehyde. The foams presented poor fire resistance indicating that, as for isocyanate based polyurethane foams, addition of a fire retardant would be necessary.

Ambient temperature self-blowing mimosa tannin-based non-isocyanate polyurethane (NIPU) rigid foam was produced, based on a formulation of tannin-based non-isocyanate polyurethane (NIPU) resin. A citric acid and glutaraldehyde mixture served as a blowing agent used to provide foaming energy and cross-link the tannin-derived products to synthesize the NIPU foams. Series of tannin-based NIPU foams containing a different amount of citric acid and glutaraldehyde were prepared. The reaction mechanism of tannin-based NIPU foams were investigated by Fourier Trasform InfraRed (FT-IR), Matrix Assisted Laser Desorption Ionization (MALDI-TOF) mass spectrometry, and ¹³C Nuclear Magnetic Resonance (¹³C NMR). The results indicated that urethane linkages were formed. The Tannin-based NIPU foams morphology including physical and mechanical properties were characterized by mechanical compression, by scanning electron microscopy (SEM), and thermogravimetric analysis (TGA). All the foams prepared showed a similar open-cell morphology. Nevertheless, the number of cell-wall pores decreased with increasing additions of glutaraldehyde, while bigger foam cells were obtained with increasing additions of citric acid. The compressive mechanical properties improved with the higher level of crosslinking at the higher amount of glutaraldehyde. Moreover, the TGA results showed that the tannin-based NIPU foams prepared had similar thermal stability, although one of them (T-Fs-7) presented the highest char production and residual matter, approaching 18.7% at 790 °C.

Soy protein isolate (SPI) and insoluble soy flour polymeric carbohydrates have been reacted with sodium periodate for the specific oxidation of vicinal –OH groups to investigate the reactions involved in this approach to soy flour adhesives. The reactions have been shown to generate carbohydrate oligomer fractions presenting one, two or multiple aldehyde groups. With the exception of the small molecular weight heptanedial, the smaller molecular weight aldehydes generated from mono- and disaccharides by the same reaction do not appear to form from the insoluble soy flour carbohydrates, or have already reacted. The reaction of periodate with soy protein isolate has been shown to generate some aldehydes too. When the mix of SPI and soy insoluble carbohydrates is treated with periodate, the majority of the observed aldehyde carrying species appear to be higher molecular weight carbohydrate oligomer fractions.