The reaction of citric acid with wood veneers was studied by Cross Polarization Magic Angle Spinning Nuclear Magnetic Resonance (CP MAS ¹³C NMR) and matrix assisted laser desorption ionization time of flight (MALDI ToF) mass spectrometry. The analysis showed that reactions of citric acid occurred with both lignin and carbohydrate constituents of wood. The reactions occurring are esterifications between the carboxylic acid functions of citric acid and the numerous aromatic and aliphatic hydroxyl groups of the main wood constituents. Reaction of citric acid with glucose as a simple model compound of carbohydrates hydroxyl groups also yielded reactions leading to linear and branched oligomers by esterification. The result indicate that the reactions of esterification are accompanied in parallel by some internal rearrangements of lignin. The applied results on bonding wide flat wood surfaces such as veneers to obtain LVL panels yielded excellent strength results even if the conditions of pressing were more drastic than what is usual for this application. The applied bonding results have shown that citric acid has great potential to be used as a bio-binder for wood veneers.

A partially biobased self-blowing and self-hardening polyurethane foam from glucose-based non-isocyanate polyurethanes (g-NIPU) was prepared by reaction of glucose with dimethyl carbonate and hexamethylene diamine. However, these foam types generally require a high foaming temperature. In this paper, a self-blowing foam based on g-NIPU was prepared at room temperature by using maleic acid as an initiator and glutaraldehyde as a crosslinker. Water absorption, compression resistance, and fire resistance were tested. Scanning electron microscopy (SEM) was used to observe the foam cells structure. Middle infrared (ATR FT-MIR) and Matrix Assisted Laser Desorption Ionization Time-of-Flight (MALDI-TOF) mass spectrometry were used to help to analyze the reactions during the foaming process. The results obtained showed that self- blowing rigid foams have good compression, this being directly proportional to the foam density. Increasing the amount of glutaraldehyde or reducing maleic acid thickens the cell walls and increases the density of the foams. MALDI-TOF analysis showed that g-NIPU reacts with both maleic acid and glutaraldehyde. The foams presented poor fire resistance indicating that, as for isocyanate based polyurethane foams, addition of a fire retardant would be necessary.

(MGG’) resin adhesives for bonding wood panels were prepared by a single step procedure, namely reacting melamine with glyoxal and simultaneously with a much smaller proportion of glutaraldehyde. No formaldehyde was used. The inherent slow hardening of this resin was overcome by the addition of N-methyl-2-pyrrolidone hydrogen sulphate ionic liquid as the adhesive hardener in the glue mix. The plywood strength results obtained were comparable with those obtained with melamine–formaldehyde resins pressed under the same conditions. Matrix assisted laser desorption ionisation time of flight (MALDI ToF) and Fourier transform Infrared (FTIR) analysis allowed the identification of the main oligomer species obtained and of the different types of linkages formed, as well as to indicate the multifaceted role of the ionic liquid. These resins are proposed as a suitable substitute for equivalent formaldehyde-based resins.