The current laboratory study is evaluating the effect of hydrofluoric acid etching duration on the surface characteristics of five silica-based glass ceramics. Changes in the pore pattern, crystal structure, roughness, and wettability were compared and evaluated. Seventy-five rectangularly shaped specimens were cut from each material (IPS e-max™, Dentsply Celtra™, Vita Suprinity™, Vita mark II™, and Vita Suprinity FC™); the sectioned samples were finished, polished, and ultrasonically cleaned. Specimens were randomly assigned into study groups: control (no etching) and four experimental groups (20, 40, 80 and 160 s of etching). The etched surfaces’ microstructure including crystal structure, pore pattern, pore depth, and pore width was studied under a scanning electron microscope, and the surface roughness and wettability were analyzed using a non-contact surface profilometer and a contact angle measuring device, respectively. The results were statistically analyzed using one-way analysis of variance (ANOVA) and the post hoc Tukey’s test. The results showed a significant change in the pore number, pore pattern, crystal structure, surface roughness, and wettability with increased etching duration. Etching for a short time resulted in small pores, and etching for longer times resulted in wider, irregular grooves. A significant increase in the surface roughness and wettability was observed with an increase in the etching duration. The findings also suggested a strong association between the surface roughness and wettability.

The current study was aimed to fabricate customized root form dental implant using additive manufacturing technique for the replacement of missing teeth. The root form dental implant was designed using Geomagic™ and Magics™, the designed implant was directly manufactured by layering technique using ARCAM A2™ electron beam melting system by employing medical grade Ti-6Al-4V alloy powder. Furthermore, the fabricated implant was characterized in terms of certain clinically important parameters such as surface microstructure, surface topography, chemical purity and internal porosity. Results confirmed that, fabrication of customized dental implants using additive rapid manufacturing technology offers an attractive method to produce extremely pure form of customized titanium dental implants, the rough and porous surface texture obtained is expected to provide better initial implant stabilization and superior osseointegration.

The present in vitro study sought to determine the effects of myrrh-containing solutions on common suture materials used in periodontal surgery. Three commonly used suture materials (silk, polyglactin 910, polytetrafluoroethylene) were immersed in four thermostatically controlled experimental media to simulate daily oral rinsing activity, namely -artificial saliva, normal saline solution with 0.2% Commiphora myrrh, full-concentration (100%) Commiphora myrrh oil, and a myrrh-containing commercial mouthwash. Tensile strength was measured at the end of each day using an Instron tensile testing machine. Silk sutures were susceptible to tensile strength loss when exposed to 0.2% myrrh solution once daily for 5 days. Myrrh-containing commercial mouthwash had no effect on tensile strength, but all three suture materials lost tensile strength when exposed to 100% myrrh oil. For patients that routinely use myrrh mouthwashes postoperatively, findings of this study suggested that silk sutures might not be the optimal material choice.