50 billion cubic meters of brine every year creates ecological hazards to the environment. In order to reuse brine efficiently, rubidium and cesium were recovered in this experiment. On the other hand, the main impurities which were needed to be eliminated in brine were lithium, sodium, potassium, calcium, and magnesium. In the procedure, seawater was distilled and evaporated first to turn into simulated brine. Perchloric acid was then added into simulated brine to precipitate potassium perchlorate which could reduce the influence of potassium in the extraction procedure. After that, t-BAMBP and ammonia were separately used as extractant and stripping agent in the extraction and stripping procedures to get rubidium hydroxide solutions and cesium hydroxide solutions. Subsequently, they reacted with ammonium carbonate to get rubidium carbonate and cesium carbonate. In a nutshell, this study shows the optimal parameters of pH value to precipitate potassium perchlorate. Besides, pH value in the system, the concentration of t-BAMBP and ammonia, organic phase/aqueous phase ratio (O/A ratio), reaction time, and reaction temperature in solvent extraction step were investigated to get high purities of rubidium carbonate and cesium carbonate.

Gallium arsenide is used in semiconductor industries worldwide. Numerous waste etching solutions are produced during the processes of GaAs wafer production. Therefore, a complete and eco-friendly technology should be established to recover gallium as a gallium chloride solution and remove arsenic ion from waste GaAs etching solution. In this study, the gallium trichloride and arsenic trisulfide powders were dissolved in ammonia solutions to prepare the simulated solutions, and the pH value was adjusted to pH 2 by nitric acid. In the extraction step, the GaAs etching solutions were extracted using 0.5 M Cyanex 272 solutions in kerosene at pH 2 and 0.1 O/A ratio for 5 min. The extraction efficiency attained 77.4%, which had an optimal ratio of concentration, and the four steps extraction efficiency attained 99.5%. After extraction, iron sulfate heptahydrates were added into the raffinate, and the arsenic ions were precipitated. The removed rate attained 99.9% when the Fe/As ratio was 10. In the stripping step, the organic phase was stripped with 0.5 M hydrochloric acid at 1 O/A ratio for 3 min, and 97.5% gallium was stripped. Finally, the purity of gallium chloride solution was 99.95% and the gallium was seven times the concentration of the etching solutions.

The selective leaching of tin anode slime was extremely important in the process of the recovery of tin anode slime. With the successful leaching, the efficiency of value metals recycling was elevated obviously. Hence, the pretreatment of tin anode slime was studied in this paper by using the environmental technology and hydrometallurgical approach to achieve the goal of valuable metal recovery from traditional waste tin anode slime. It is worth noting that there are a large amount of value metals including Sn, Sb, Bi, Cu and Ag in the tin anode slime. The results indicated the optimal conditions of leaching process are 3.0 M HCl with 0.1M NaClO3 and liquid-solid mass ratio of 30 ml/g in 30 minutes at 45 degrees of Celsius and about Sn 85.32%, Sb 96.93%, Bi 97.63%. Meanwhile, silver and copper were all leached out by HCl solution in the leaching of tin anode slime.