This work reports on a comparative study comprising three transition metal oxides, MoO3, WO3 and V2O5, acting as front p-type contacts for n-type crystalline silicon heterojunction solar cells. Owing to their high work functions (>5 eV) and wide energy band gaps, these oxides act as transparent hole-selective contacts with semiconductive properties that are determined by oxygen-vacancy defects (MoO3-x), as confirmed by X-ray photoelectron spectroscopy. In the fabricated hybrid structures, 15 nm thick transition metal oxide layers were deposited by vacuum thermal evaporation. Of all three devices, the V2O5/n-silicon heterojunction performed the best with a conversion efficiency of 15.7% and an open-circuit voltage of 606 mV, followed by MoO3 (13.6%) and WO3 (12.5%). These results bring into view a new silicon heterojunction solar cell concept with advantages such as the absence of toxic dopant gases and a simplified low-temperature fabrication process.Preprin

Building blocks of life show well-defined chiral symmetry which has a direct influence on their properties and role in Nature. Chiral molecules are typically characterized by optical techniques such as circular dichroism (CD) where they exhibit signatures in the ultraviolet frequency region. Plasmonic nanostructures have the potential to enhance the sensitivity of chiral detection and translate the molecular chirality to the visible spectral range. Despite recent progress, to date, it remains unclear which properties plasmonic sensors should exhibit to maximize this effect and apply it to reliable enantiomer discrimination. Here, we bring further insight into this complex problem and present a chiral plasmonic sensor composed of a racemic mixture of gammadions with no intrinsic CD, but high optical chirality and electric field enhancements in the near-fields. Owing to its unique set of properties, this configuration enables us to directly differentiate phenylalanine enantiomers in the visible frequency range.

Transition metal oxides (TMOs) have recently been proved to efficiently serve as hole-selective contacts in crystalline silicon (c-Si) heterojunction solar cells. In the present work, two TMO/c-Si heterojunctions are explored using MoO3 (reference) and V2O5 as an alternative candidate. It has been found that V2O5 devices present larger (16% improvement) power conversion efficiency mainly due to their higher open-circuit voltage. While V2O5/c-Si devices with textured front surfaces exhibit larger short-circuit currents, it is also observed that flat solar cell architectures allow for passivation of the V2O5/n-Si interface, giving significant carrier lifetimes of 200 µs (equivalent to a surface recombination velocity of Seff ~140 cm s-1) as derived from impedance analysis. As a consequence, a significant open-circuit voltage of 662 mV is achieved. It is found that, at the TMO/c-Si contact, a TMO work function enhancement ¿FTMO occurs during the heterojunction formation with the consequent dipole layer enlargement ¿’=¿+¿FTMO. Our results provide new insights into the TMO/c-Si contact energetics, carrier transport across the interface and surface recombination allowing for further understanding of the nature of TMO/c-Si heterojunctions.Peer ReviewedPostprint (published version