Rare-earth doped oxyfluoride glass ceramics represent a new generation of tailorable optical materials with high potential for optical-related applications such as optical amplifiers, optical waveguides, and white LEDs. Their key features are related to the high transparency and remarkable luminescence properties, while keeping the thermal and chemical advantages of oxide glasses. Sol-gel chemistry offers a flexible synthesis approach with several advantages, such as lower processing temperature, the ability to control the purity and homogeneity of the final materials on a molecular level, and the large compositional flexibility. The review will be focused on optical properties of sol-gel derived nano-glass ceramics related to the RE-doped luminescent nanocrystals (fluorides, chlorides, oxychlorides, etc.) such as photoluminescence, up-conversion luminescence, thermoluminescence and how these properties are influenced by their specific processing, mostly focusing on the findings from our group and similar ones in the literature, along with a discussion of perspectives, potential challenges, and future development directions.

This work investigates the structural, magnetic and magneto-optical properties of a new zinc phosphate-tellurite glass belonging to the 45ZnO-10Al₂O₃-40P₂O₅-5TeO₂ system. The glass was prepared by a wet method of processing the starting reagents followed by suitable melting–stirring–quenching–annealing steps. Specific parameters such as density, average molecular mass, molar volume, oxygen packaging density, refractive index, molar refractivity, electronic polarizability, reflection loss, optical transmission, band gap and optical basicity have been reported together with thermal, magnetic and magneto-optical characteristics. Absorption bands appear in the blue and red visible region, while over 600 nm the glass becomes more transparent. FTIR and Raman spectra evidenced phosphate-tellurite vibration modes proving the P₂O₅ and TeO₂ network forming role. Magnetic measurements reveal the diamagnetic character of the Te-doped glass with an additional weak ferromagnetic signal, specific to diluted ferromagnetic oxides. Positive Faraday rotation angle with monotonous decreasing value at increasing wavelength was evidenced from magneto-optical measurements. The final product is a composite material comprising of a non-crystalline vitreous phase and Te-based nanoclusters accompanied by oxygen vacancies. The metallic-like Te colloids are responsible for the dark reddish color of the glass whereas the accompanying oxygen vacancies might be responsible for the weak ferromagnetic signal persisting up to room temperature.

In this work, new films containing composite materials based on blends of thermoplastic polymers of the polyurethane (TPU) and polyolefin (TPO) type, in the absence and presence of BaTiO₃ nanoparticles (NPs) with the size smaller 100 nm, were prepared. The vibrational properties of the free films depending on the weight ratio of the two thermoplastic polymers were studied. Our results demonstrate that these films are optically active, with strong, broad, and adjustable photoluminescence by varying the amount of TPU. The crystalline structure of BaTiO₃ and the influence of thermoplastic polymers on the crystallization process of these inorganic NPs were determined by X-ray diffraction (XRD) studies. The vibrational changes induced in the thermoplastic polymer’s matrix of the BaTiO₃ NPs were showcased by Raman scattering and FTIR spectroscopy. The incorporation of BaTiO₃ NPs in the matrix of thermoplastic elastomers revealed the shift dependence of the photoluminescence (PL) band depending on the BaTiO₃ NP concentration, which was capable of covering a wide visible spectral range. The dependencies of the dielectric relaxation phenomena with the weight of BaTiO₃ NPs in thermoplastic polymers blends were also demonstrated.

This study explored a new green approach of the wet ferritization method to obtain magnetic cobalt ferrite (CoFe₂O₄) by using eucalyptus leaves aqueous extract as a reducing/chelating/capping agent. The spinel single cubic phases of prepared samples were proved by powder X-ray diffraction (XRD), Fourier-Transform Infrared (FTIR) and Raman spectroscopy. The average crystallite size is in the range between 3 and 20 nm. The presence of the functional groups coating the obtained material is confirmed from FTIR and thermal analysis. The scanning electron microscopy (SEM) analysis showed a morphology consisting of nanoparticle aggregates. Raman spectroscopy detects the characteristic bands of spinel-type CoFe₂O₄. Magnetic investigations reveal the formation of ferromagnetic compounds with cubic magnetic anisotropy and a blocking temperature around 140 K, specific for this type of material. The biosynthesized CoFe₂O₄ could be an attractive candidate for biomedical applications, exhibiting promising antimicrobial and antibiofilm activity, particularly against Gram-negative bacteria and fungal strains.

In this study, we report on the structural, magnetic, and optical properties of Tb³⁺-doped CeF₃ nanocrystals prepared via a polyol-assisted route, followed by calcination. X-ray diffraction analysis and electron microscopy investigations have shown the formation of a dominant Ce_0.75F₃ nanocrystalline phase (of about 99%), with a relatively uniform distribution of nanocrystals about 15 nm in size. Magnetization curves showed typical paramagnetic properties related to the presence of Ce³⁺ and Tb³⁺ ions. The magnetic susceptibility showed a weak inflexion at about 150 K, assigned to the cerium ions’ crystal field splitting. Under UV light excitation of the Ce³⁺ ions, we observed Tb³⁺ green luminescence with a quantum yield of about 20%.

IV-VI semiconductor quantum dots embedded into an inorganic matrix represent nanostructured composite materials with potential application in temperature sensor systems. This study explores the optical, structural, and morphological properties of a novel PbS quantum dots (QDs)-doped inorganic thin film belonging to the Al₂O₃-SiO₂-P₂O₅ system. The film was synthesized by the sol-gel method, spin coating technique, starting from a precursor solution deposited on a glass substrate in a multilayer process, followed by drying of each deposited layer. Crystalline PbS QDs embedded in the inorganic vitreous host matrix formed a nanocomposite material. Specific investigations such as X-ray diffraction (XRD), optical absorbance in the ultraviolet (UV)-visible (Vis)-near infrared (NIR) domain, NIR luminescence, Raman spectroscopy, scanning electron microscopy–energy dispersive X-ray (SEM-EDX), and atomic force microscopy (AFM) were used to obtain a comprehensive characterization of the deposited film. The dimensions of the PbS nanocrystallite phase were corroborated by XRD, SEM-EDX, and AFM results. The luminescence band from 1400 nm follows the luminescence peak of the precursor solution and that of the dopant solution. The emission of the PbS-doped film in the NIR domain is a premise for potential application in temperature sensing systems.