One of the fundamental issues in the Fused Filament Fabrication (FFF) additive manufacturing process lies in the mechanical property anisotropy where the strength of the FFF-3D printed part in the build-direction can be significantly lower than that in other directions. The physical phenomenon that governs this issue is the coupled effect of macroscopic thermal mechanical issues associated with the thermal history of the interface, and the microscopic effect of the polymer microstructure and mass transfer across interfaces. In this study it was found that the use of 34.4 kHz ultrasonic vibrations during FFF-3D printing results in an increase of up to 10% in the interlayer adhesion in Acrylonitrile Butadiene Styrene (ABS), comparing the printing in identical thermal conditions to that in conventional FFF printing. This increase in the interlayer adhesion strength is attributed to the increase in polymer reptation due to ultrasonic vibration-induced relaxation of the polymer chains from secondary interactions in the interface regions.

Extrusion-based polymer 3D printing induces shear strains within the material, influencing its rheological and mechanical properties. In materials like polyvinylidene difluoride (PVDF), these strains stretch polymer chains, leading to increased crystallinity and improved piezoelectric properties. This study demonstrates a 400% enhancement in the piezoelectric property of extrusion-printed PVDF by introducing additional shear strains during the printing process. The continuous torsional shear strains, imposed via a rotating extrusion nozzle, results in additional crystalline β-phases, directly impacting the piezoelectric behavior of the printed parts. The effect of the nozzle’s rotational speed on the amount of β-phase formation is characterized using FTIR. This research introduces a new direction in the development of polymer and composite 3D printing, where in-process shear strains are used to control the alignment of polymer chains and/or in-fill phases and the overall properties of printed parts.

Fused filament fabrication is one of the most desired thermal plastic additive manufacturing processes because of its ability to fabricate complex objects with high accessibility. However, due to the extrusion track-based direct write process mechanism, parts built using this method exhibit anisotropic mechanical properties. In this work, an in-process laser heating method is introduced to heal interface adhesion between adjacent deposited tracks by increasing the interface temperature to promote polymer reptation and enhance bonding strength of the interface of adjacent tracks. With the use of laser heating induced interface healing, the measured flexural strength between adjacent tracks in the same layer increased and exceeded that of the control sample tested along the track direction. The effect of laser on interface healing was also verified by investigating the load–displacement curve and morphology analysis of the fractured surface.

Material extrusion-based polymer 3D printing, one of the most commonly used additive manufacturing processes for thermoplastics and composites, has drawn extensive attention due to its capability and cost effectiveness. However, the low surface finish quality of the printed parts remains a drawback due to the nature of stacking successive layers along one direction and the nature of rastering of the extruded tracks of material. In this work, an in-process thermal radiation-assisted, surface reflow method is demonstrated that significantly improves the surface finish of the sidewalls of printed parts. It is observed that the surface finish of the printed part is drastically improved for both flat and curved surfaces. The effect of surface reflow on roughness reduction was characterized using optical profilometry and scanning electron microscopy (SEM), while the local heated spot temperature was quantified using a thermal camera.