Titanium and its alloys are widely used for dental and medical biomaterials due to their excellent mechanical and biological advantages. After the introduction of direct laser metal sintering (DLMS) 3D printing technology and its use over conventional machine-cut processes, questions remain regarding whether 3D-printed titanium (alloy) devices have similar biological properties to machine-cut counterparts for dental applications. Thus, this work focuses on comparing the biological activities of machine-cut and 3D-printed specimens after optimizing the DLMS 3D-printing conditions in terms of the mechanophysical characteristics. The DLMS 3D-printing (as a function of the laser spacing from 30-100μm) and post-surface treatment (as-given or sand-blasted) conditions were optimized using medical-grade Ti-6Al-4V powders in terms of the inner pore amount, mechanical properties, roughness and hydrophilicity. Then, the initial cell adhesion of the optimized DLMS 3D-printed Ti-6Al-4V specimen was compared with that of the machine-cut Ti-6Al-4V specimen against human dermal fibroblasts (hDFs) and mesenchymal stem cells (hMSCs), which are representative of direct-contact cell types of orofacial mucosa and bone, respectively. hMSC differentiation on the specimens was conducted for up to 21 days to measure the osteogenic gene expression and biomineralization. Laser spacings of 30-40μm had fewer inner defects and consequently a higher three-point flexural strength and elastic modulus compared to other larger laser spacings. Depending on the span width (0.3-1mm) in the lattice architecture, the elastic modulus of the 3D-printed cuboid specimen can be further controlled (up to ∼30 times). The sand-blasted specimens after 3D printing revealed lower surface roughness and higher hydrophilicity compared to the as-3D printed specimen, which were considered optimal conditions for biological study. Initial hDF and hMSC adhesion for 12 hr and hMSC differentiation on the surface were comparable between the sand-blasted 3D-printed and machine-cut specimens in terms of adherent cell numbers, vinculin intensity, osteogenic gene expression and biomineralization. The optimized DLMS 3D-printed Ti-6Al-4V specimen had similar biological properties to those of the machine-cut counterpart, suggesting the potential usefulness of 3D printing technology for a wide range of dental applications.

Recently, bioactive glass nanoparticles (BGns) have been acknowledged for their ability to promote interactions with the periapical tissue and enhance tissue regeneration by releasing therapeutic ions. However, there have been no studies on calcium silicate sealers with bioactive glass nanoparticle (BGn) additives. In the present study, a premixed calcium silicate root canal sealer reinforced with BGn (pre-mixed-RCS@BGn) was developed and its physicochemical features and biological effects were analyzed. Three specimens were in the trial: 0%, 0.5%, and 1% bioactive glass nanoparticles (BGns) were gradually added to the premixed type of calcium silicate-based sealer (pre-mixed-RCS). To elucidate the surface properties, scanning electron microscopy, X-ray diffraction, and energy-dispersive spectroscopy were used and flowability, setting time, solubility, and radiopacity were analyzed to evaluate the physical properties. Chemical properties were investigated by water contact angle, pH change, and ion release measurements. The antibacterial effects of the bioactive set sealers were tested with Enterococcus faecalis and the viability of human bone marrow-derived mesenchymal stem cells (hMSCs) with this biomaterial was examined. In addition, osteogenic differentiation was highly stimulated, which was confirmed by ALP (Alkaline phosphatase) activity and the ARS (Alizarin red S) staining of hMSCs. The pre-mixed-RCS@BGn satisfied the ISO standards for root canal sealers and maintained antimicrobial activity. Moreover, pre-mixed-RCS@BGn with more BGns turned out to have less cytotoxicity than pre-mixed-RCS without BGns while promoting osteogenic differentiation, mainly due to calcium and silicon ion release. Our results suggest that BGns enhance the biological properties of this calcium silicate-based sealer and that the newly introduced pre-mixed-RCS@BGn has the capability to be applied in dental procedures as a root canal sealer. Further studies focusing more on the biocompatibility of pre-mixed-RCS@BGn should be performed to investigate in vivo systems, including pulp tissue.

Masticatory muscles are closely involved in mastication, pronunciation, and swallowing, and it is therefore important to study the specific functions and dynamics of the mandibular and masticatory muscles. However, the shortness of muscle fibers and the diversity of movement directions make it difficult to study and simplify the dynamics of mastication. The purpose of this study was to use 3-dimensional (3D) simulation to observe the functions and movements of each of the masticatory muscles and the mandible while chewing. To simulate the masticatory movement, computed tomographic images were taken from a single Korean volunteer (30-year-old man), and skull image data were reconstructed in 3D (Mimics; Materialise, Leuven, Belgium). The 3D-reconstructed masticatory muscles were then attached to the 3D skull model. The masticatory movements were animated using Maya (Autodesk, San Rafael, CA) based on the mandibular motion path. During unilateral chewing, the mandible was found to move laterally toward the functional side by contracting the contralateral lateral pterygoid and ipsilateral temporalis muscles. During the initial mouth opening, only hinge movement was observed at the temporomandibular joint. During this period, the entire mandible rotated approximately 13 degrees toward the bicondylar horizontal plane. Continued movement of the mandible to full mouth opening occurred simultaneously with sliding and hinge movements, and the mandible rotated approximately 17 degrees toward the center of the mandibular ramus. The described approach can yield data for use in face animation and other simulation systems and for elucidating the functional components related to contraction and relaxation of muscles during mastication.

Studies related to facial soft tissue thickness (FSTT) have been conducted since the late 19th century. Soft tissue is any tissue in the body that is not hardened by ossification or calcification processes, such as bones and teeth; and varies according to sex, age, race, and nutritional status. Forensically, soft tissue thickness plays an important role in cases where a cadaver has no unique characteristics; and the remains cannot be identified through DNA analysis, fingerprints, or examination of dental records. Therefore, the results of the current study suggest that the average thickness of the three skeletal classes (i.e., straight, concave, and convex) should be used for face restoration and forensic art research. It is thought that the current study’s results will be invaluable in the fields of forensic science, forensic art, anthropology, and dentistry. As a result, gender differences were observed in all classes, and the facial tissue thickness in Korean adults differed according to gender and occlusion type.

The maxillary sinus growth is initiated 3 months after birth, and it grows lateral and inferior until the pneumatization of the alveolar bone occurs. The facial skeleton has recently been determined as affecting the maxillary sinus, prompting additional studies on changes in the size of the maxillary sinus. This study aimed to determine the size of the maxillary sinus using a 3D program after categorizing South Korean adults according to their facial index (FI) classification. The participants of this study were 60 patients in their 20s, who visited the orthodontic department of Dankook University Dental Hospital (approval no. DUDH IRB 2015-12-022). The CBCT of the patients were extracted and measured as 3D images using Mimics (version 22.0, Materialise, Leuven, Belgium). Upon categorizing the subjects based on their FI classification, they were grouped into the mesoprosopic, leptoprosopic, and hyperleptoprosopic types. A one-way ANOVA was performed to evaluate the mean differences of the maxillary sinus, depending on the FI classification. In this study, the maxillary sinus tended to be wider in those with mesoprosopic type, and tended to be higher in the hyperleptoprosopic type, suggesting a need for clinicians to focus to the shape of the face during clinical treatments.

Park SB, et al. J Periodontal Implant Sci. 2017 Jun;47(3):154-164. https://doi.org/10.5051/jpis.2017.47.3.154