This study describes the surface topography of the 17-4 PH stainless steel machined under dry, wet and near-dry cutting conditions. Cutting speeds of 150–500 m/min, feeds of 0.05–0.4 mm/rev and 0.5 mm depth of cutting were applied. The research was based on the ‘parameter space investigation’ method. Surface roughness parameters, contour maps and material participation curves were analysed using the optical Sensofar S Neox 3D profilometer and the effect of feed, cutting speed and their mutual interaction was noticed. Changes in chip shape depending on the processing conditions are shown. Compared to dry machining, a reduction of Sa, Sq and Sz parameters of 38–48% was achieved for near-dry condition. For lower feeds and average cutting speeds valleys and ridges were observed on the surface machined under dry, wet and near-dry conditions. For higher feeds and middle and higher cutting speeds, deep valleys and high ridges were observed on the surface. Depending on the processing conditions, different textures of the machined surface were registered, particularly anisotropic mixed, periodic and periodically determined. In the Sa range of 0.4–0.8 μm for dry and wet conditions the surface isotropy is ~20%, under near-dry conditions it is ~60%.

The influence of cooling conditions and surface topography after finish turning of Ti6Al4V titanium alloy on corrosion resistance and surface bioactivity was analyzed. The samples were machined under dry and minimum quantity lubrication (MQL) conditions to obtain different surface roughness. The surface topographies of the processed samples were assessed and measured using an optical profilometer. The produced samples were subjected to electrochemical impedance spectroscopy (EIS) and corrosion potential tests (E_corr) in the presence of simulated body fluid (SBF). The surface bioactivity of the samples was assessed on the basis of images from scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) analysis. The inspection of the surfaces of samples after turning under dry and MQL conditions revealed unevenly distributed precipitation of hydroxyapatite compounds (Ca/P) with a molar ratio in the range of 1.73–1.97. Regardless of the cutting conditions and surface roughness, the highest values of E_corr ~0 mV were recorded on day 7 of immersion in the SBF solution. The impedance characteristics showed that, compared to the MQL conditions, surfaces machined under dry conditions were characterized by greater resistance and the presence of a passive layer on the processed surface. The main novelty of the paper is the study of the effect of ecological machining conditions, namely, dry and MQL cutting on the corrosion resistance and surface bioactivity of Ti6Al4V titanium alloy after finish turning. The obtained research results have practical significance. They can be used by engineers during the development of technological processes for medical devices made of Ti6Al4V alloy to obtain favorable functional properties of these devices.

This paper analyses three components of total cutting force and chip shape changes when finish turning 17-4 PH (precipitation hardening) stainless steel. A Finite Element Method (FEM) simulation of cutting forces was also performed using the Johnson–Cook constitutive model. The results were compared with those obtained from experimental studies. Variable feeds of 0.05–0.4 mm/rev and depth of cut of 0.2–1.2 mm with a cutting speed of 220 m/min were used. The studies were carried out under dry and wet cooling conditions and with the use of minimum quantity lubrication (MQL). This research was realized based on the Parameter Space Investigation (PSI) method. Statistical analysis of the obtained results was carried out using Statistica-13 software. It was found that the cutting force F_c and feed force F_f depend on the depth of cut and feed, and the passive force F_p depends mainly on the feed. Compared to dry cutting conditions, a reduction of 43% and 39% of the cutting force F_c was achieved for wet machining and MQL machining, respectively. Regardless of the cooling conditions, a favorable chip shape was registered for a_p = 1–1.1 mm and f = 0.25–0.3 mm/rev. Compared to the experimental studies, the FEM simulation showed differences of ~13% for the cutting force F_c and of ~36% for the feed force F_f.

The paper presents evaluation of the surface topography obtained after turning of AISI 1045 steel with the use of cemented carbide tools diversified in terms of applied titanium-based coatings. During the research, three types of coatings deposited with the PVD method on a P25 sintered carbide...

Titanium alloys, particularly Ti-6Al-4V, are widely used in many industries due to their high strength, low density, and corrosion resistance. However, machining these materials is challenging due to high strength at elevated temperatures, low thermal conductivity, and high chemical reactivity. This study investigates Recurrence Plot (RP) and Recurrence Quantification Analysis (RQA) to analyze tool wear during the finish turning of Ti-6Al-4V. The tests were conducted under Minimum Quantity Lubrication (MQL). Three inserts (two coated, one uncoated) were tested, and tool life was evaluated based on material removal volume. The issue of tool exploitation and process reliability is crucial, as it directly impacts machining performance. Results show that the uncoated insert outperformed the coated ones. RQA parameters indicated a stable-to-unstable transition in coated inserts but not in the uncoated insert. This suggests that recurrence analysis can monitor cutting dynamics in coated insert machining, but further research is needed for uncoated tools. This paper’s novelty lies in applying RP and RQA to diagnose tool wear in titanium alloy machining under MQL conditions, a method not previously explored in this context.

Industrial practitioners are working on predictive solutions for the precise evaluation of input parameters and processed surfaces of engineering materials. To aid the aeronautical industry, this study is an effort to develop the mathematical modelling for comprehensive surface analysis of input parameters and surface finish after dry machining of CLARM HBR, a steel alloy with attractive mechanical properties and wide applications in large caliber gun barrels and high-pressure vessels. Feed rate, rotational speed, and depth of cut were taken as quantitative parameters, whereas machining time was considered as a categorical factor with a classification of three levels. Response surface methodology (RSM) with a central component design has been used for the constitution of the experimental design, mathematical modelling, and analysis of developed models. Eighteen samples were prepared to perform the experimentation for the development of prediction models. The adequacy of the developed models was verified using analysis of variance (ANOVA), and the models were validated using confirmatory trial experiments, which revealed the experimental results agreeing with predictions. The feed rate was the most significant parameter in achieving the desired surface finish. An increase in rotational speed at a low feed rate resulted in very fine surface texture, as though it deteriorated the surface finish at higher feed rates. The superior surface quality obtained was 0.137 μm at parametric settings of 0.19 mm/rev feed, 90 rpm speed, 3 mm depth of cut, and 4 min time. Overall, higher values of surface roughness were frecorded in the third level of process variable time. The developed empirical models are expected to aid manufacturers and machining practitioners in the prediction of the desired surface finish concerning different parameters before the experimentations.