Limnophila aromatica is commonly used as a spice and a medicinal herb in Southeast Asia. In this study, water and various concentrations (50%, 75%, and 100%) of methanol, ethanol, and acetone in water were used as solvent in the extraction of L. aromatica. The antioxidant activity, total phenolic content, and total flavonoid content of the freeze-dried L. aromatica extracts were investigated using various in vitro assays. The extract obtained by 100% ethanol showed the highest total antioxidant activity, reducing power and DPPH (2,2-diphenyl-1-picrylhydrazyl) radical scavenging activity. The same extract also exhibited the highest phenolic content (40.5 mg gallic acid equivalent/g of defatted L. aromatica) and the highest flavonoid content (31.11 mg quercetin equivalent/g of defatted L. aromatica). The highest extraction yield was obtained by using 50% aqueous acetone. These results indicate that L. aromatica can be used in dietary applications with a potential to reduce oxidative stress.

A greener route to synthesize mesoporous copper–gallic acid metal–organic framework (CuGA MOF) than the conventional method using harmful DMF solvent was proposed in this study. Various synthesis attempts were conducted by modifying the synthesis conditions to produce CuGA MOF with comparable physical properties to a reference material (DMF-synthesized CuGA NMOF). The independent variables investigated include the molar ratio of NaOH to GA (1.1 to 4.4) and the synthesis temperature (30, 60, 90 °C). It was found that proper NaOH addition was crucial for suppressing the generation of copper oxide while maximizing the formation of CuGA MOF. On the other hand, the reaction temperature mainly affected the stability and adsorption potential of CuGA MOF. Reacting Cu, GA, and NaOH at a molar ratio of 1:1:2.2 and a temperature of 90 °C, produced mesoporous MOF (CuGA 90–2.2) with a surface area of 198.22 m²/g, a pore diameter of 8.6 nm, and a thermal stability of 219 °C. This MOF exhibited an excellent adsorption capacity for the removal of methylene blue (124.64 mg/g) and congo red (344.54 mg/g). The potential usage of CuGA 90–2.2 as a reusable adsorbent was demonstrated by its high adsorption efficiency (> 90%) after 5 adsorption–desorption cycles.