Micro-turning is a micro-mechanical cutting method used to produce small diameter cylindrical parts. Since the diameter of the part is usually small, it may be a little difficult to improve the surface quality by a second operation, such as grinding. Therefore, it is important to obtain the good surface finish in micro turning process using the ideal cutting parameters. Here, the multi-objective optimization of micro-turning process parameters such as cutting speed, feed rate and depth of cut were performed by response surface method (RSM). Two important machining indices, such as surface roughness and material removal rate, were simultaneously optimized in the micro-turning of a Ti6Al4V alloy. Further, the scanning electron microscope (SEM) analysis was done on the cutting tools. The overall results depict that the feed rate is the prominent factor that significantly affects the responses in micro-turning operation. Moreover, the SEM results confirmed that abrasion and crater wear mechanism were observed during the micro-turning of a Ti6Al4V alloy.

Together, 316L steel, magnesium-alloy, Ni-Ti, titanium-alloy, and cobalt-alloy are commonly employed biomaterials for biomedical applications due to their excellent mechanical characteristics and resistance to corrosion, even though at times they can be incompatible with the body. This is attributed to their poor biofunction, whereby they tend to release contaminants from their attenuated surfaces. Coating of the surface is therefore required to mitigate the release of contaminants. The coating of biomaterials can be achieved through either physical or chemical deposition techniques. However, a newly developed manufacturing process, known as powder mixed-electro discharge machining (PM-EDM), is enabling these biomaterials to be concurrently machined and coated. Thermoelectrical processes allow the migration and removal of the materials from the machined surface caused by melting and chemical reactions during the machining. Hydroxyapatite powder (HAp), yielding Ca, P, and O, is widely used to form biocompatible coatings. The HAp added-EDM process has been reported to significantly improve the coating properties, corrosion, and wear resistance, and biofunctions of biomaterials. This article extensively explores the current development of bio-coatings and the wear and corrosion characteristics of biomaterials through the HAp mixed-EDM process, including the importance of these for biomaterial performance. This review presents a comparative analysis of machined surface properties using the existing deposition methods and the EDM technique employing HAp. The dominance of the process factors over the performance is discussed thoroughly. This study also discusses challenges and areas for future research.

A combined analytical and experimental study was carried out to analyze the effects of cryogenic cooling on temperature during turning of AZ31C magnesium alloy. Finite element method was employed to model and simulating the cryogenic and dry turning. Results obtained from the model were found to be in good agreement with the experimental observations. For the maximum temperature at the turned surface, the difference in the experimental and predicted value observed during dry and cryogenic turning was only 4 and 8% respectively. A significant reduction in the maximum temperature on the chip surface (around 35%) and tool surface (around 29%) was observed during the cryogenic turning compared to dry turning. This reduction in temperature was an attribute of liquid nitrogen, which produces intense cooling effect around the vicinity cutting zone where heat generation takes place hence enhancing the heat transfer. The isothermal region belonging to the highest temperature on the tool surface was also reduced by about 42%. The reduction in temperature during cryogenic conditions were found to be beneficial for the machining of magnesium alloys under safe conditions, reducing the risk of ignition and explosions, and also increases the sustainability of the process.