A RL-CNP with excellent wet strength and water stability was developed by using activated residual lignin as a reinforcement.

Due to the natural cellulose encapsulated in both lignin and hemicellulose matrices, as well as in plant cell walls with a compact and complex hierarchy, extracting cellulose nanofibers (CNFs) from lignocellulosic biomass is challenging. In this study, a sustainable high yield strategy with respect to other CNF preparations was developed. The cellulose was liberated from plant cell walls and fibrillated to a 7–22 nm thickness in one bath treatment with H₃PO₄ and H₂O₂ under mild conditions. The cellulose underwent swelling, the lignin underwent oxidative degradation, and the hemicellulose and a small amount of cellulose underwent acid hydrolysis. The CNFs’ width was about 12 nm, with high yields (93% and 50% based on cellulose and biomass, respectively), and a 64% crystallinity and good thermal stability were obtained from bagasse. The current work suggests a strategy with simplicity, mild conditions, and cost-effectiveness, which means that this method can contribute to sustainable development for the preparation of CNFs.