Due to the natural cellulose encapsulated in both lignin and hemicellulose matrices, as well as in plant cell walls with a compact and complex hierarchy, extracting cellulose nanofibers (CNFs) from lignocellulosic biomass is challenging. In this study, a sustainable high yield strategy with respect to other CNF preparations was developed. The cellulose was liberated from plant cell walls and fibrillated to a 7–22 nm thickness in one bath treatment with H₃PO₄ and H₂O₂ under mild conditions. The cellulose underwent swelling, the lignin underwent oxidative degradation, and the hemicellulose and a small amount of cellulose underwent acid hydrolysis. The CNFs’ width was about 12 nm, with high yields (93% and 50% based on cellulose and biomass, respectively), and a 64% crystallinity and good thermal stability were obtained from bagasse. The current work suggests a strategy with simplicity, mild conditions, and cost-effectiveness, which means that this method can contribute to sustainable development for the preparation of CNFs.

The significant challenges in the use of cellulose as a replacement for plastic are its mechanical properties’ degradation and uncontrolled deformation during the rewetting process. Herein, inspired by the reinforcement of cellulose by lignin in natural plant tissue, a strong and water-stable lignin–cellulose composite (LCC) was developed. A nanocellulose hybrid lignin complex (CHLC) created from bagasse residue after enzymatic hydrolysis was added into a pulp of bleached fibre extracted from pine to produce a lignin–cellulose sheet. The lignin as a water-stable reinforcing matrix, via the hydrogen bonding of the nanocellulose in the CHLC with the fibre was efficiently introduced onto the fibres and the fibre network voids. Compared with a typical lignin-free cellulose sheet, the dry strength and wet strength of the LCC were 218% and 2233% higher, respectively. The developed LCC is an eco-friendly and biodegradable alternative to plastic.

Separating the fibers, deconstructing both the interlamellar structures and the intermicrofibrils structures in the cell wall, and cleaving the amorphous regions of cellulose (all reached in one bath chemical-assisted treatment), then extracting cellulose nanofibers (CNFs) from biomass, is both challenging and imperative. A simple, cost-effective and green strategy for extracting CNFs from bamboo using nitric acid and hydrogen peroxide (NCHP), to enable fibrillation via a cooperative mechanism, is demonstrated herein. NCHP-CNFs 13.1 ± 2.0 nm wide, with a high aspect ratio, 74% crystallinity, excellent UV resistance and high thermal stability, were successfully extracted by treatment in HNO₃ aqueous solution, at a concentration of 3.2 mol/L, and treatment with 60.00 mmol/g H₂O₂ at 50 °C for 48 h. The yields of NCHP-CNFs reached 73% and 99% based on biomass and cellulose, respectively, due to the high delignification selectivity of OH⁺ and the mild aqueous conditions during the NCHP treatment. These NCHP-CNFs with excellent UV resistance can potentially be applied in the field of UV-resistant coatings, to replace organic and inorganic materials.