In this study, precursor molecules based on PEG/PPG and polydimethylsiloxane (PDMS), both widely used rubbery polymers, were copolymerized with bulky adamantane into copolymer membranes. Ring-opening metathesis polymerization (ROMP) was employed during the polymerization process to create a structure with both ends crosslinked. The precursor molecules and corresponding polymer membranes were characterized using various analytical methods. The polymer membranes were fabricated using different compositions of PDMS and adamantane, to determine how the network structure affected their gas separation performance. PEG/PPG, in which CO₂ is highly soluble, was copolymerized with PDMS, which has high permeability, and adamantane, which controlled the crosslinking density with a rigid and bulky structure. It was confirmed that the resulting crosslinked polymer membranes exhibited high solubility and diffusivity for CO₂. Further, their crosslinked structure using ROMP technique made it possible to form good films. The membranes fabricated in the present study exhibited excellent performance, i.e., CO₂ permeability of up to 514.5 Barrer and CO₂/N₂ selectivity of 50.9.

A series of CO₂-selective polyimides (CE-PDMS-PI-x) was synthesized by copolymerizing crown ether diamine (trans-diamino-DB18C6) and PDMS-diamine with 4,4′-(hexafluoroisopropylidene) di-phthalic anhydride (6FDA) through the polycondensation reaction. The structural characteristics of the copolymers and corresponding membranes were characterized by nuclear magnetic resonance (NMR), infrared spectroscopy (ATR-FTIR), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), X-ray diffraction (XRD), and gel permeation chromatography (GPC). The effect of PDMS loading on the CE-PDMS-PI-x copolymers was further analyzed and a very good structure–property relationship was found. A well-distributed soft PDMS unit played a key role in the membrane’s morphology, in which improved CO₂-separation performance was observed at a low PDMS content (5 wt %). In contrast, the fine-grained phase separation adversely affected the separation behavior at a certain level of PDMS loading, and the PDMS was found to provide a flexible gas-diffusion path, affecting only the permeability without changing the selective gas-separation performance for the copolymers with a PDMS content of 20% or above.