We studied the influences of the thickness of the porous silicon layer and the conductivity type on the porous silicon sensors response when exposed to ethanol vapor. The response was determined at room temperature (27 ${}^{\circ }$C) in darkness using a horizontal aluminum electrode pattern. The results indicated that the intensity of the response can be directly or inversely proportional to the thickness of the porous layer depending on the conductivity type of the semiconductor material. The response of the porous sensors was similar to the metal oxide sensors. The results can be used to appropriately select the conductivity of semiconductor materials and the thickness of the porous layer for the target gas.

The effect of the deposit temperature of zinc oxide (ZnO) doped with nickel (Ni) by hot filament chemical vapor deposition (HFCVD) technique is reported in this work. The technique allows depositing ZnO:Ni in short intervals (1 min). A deposit of undoped ZnO is used as a reference sample. The reference sample was deposited at 500 °C. The ZnO:Ni samples were deposited at 500 °C, 400 °C, 350 °C, and 300 °C. The samples were studied using structural, morphological, and optical characterization techniques. The Ni incorporation to the ZnO lattice was verified by the shift of the X-ray diffraction peaks, the Raman peaks, the band gap, and the photoluminescence measurements. It was found that the deposit temperature affects the structural, morphological, and optical properties of the ZnO:Ni samples too. The structure of the ZnO:Ni samples corresponds to the hexagonal structure. Different microstructures shapes such as spheres, sea urchins, and agglomerate were found in samples; their change is attributed to the deposit temperature variation. The intensity of the photoluminescence of the ZnO:Ni improves concerning the ZnO due to the Ni incorporation, but it decreases as the deposit temperature decreases.

In this work, we report a green synthesis of zinc oxide (ZnO) nanoparticles using aqueous and ethanolic extracts of Tradescantia spathacea (purple maguey) as bioreducing and stabilizing agents, which are plant extracts not previously employed for metal oxide nanoparticle synthesis. This method provides an efficient, eco-friendly, and reproducible route to obtain ZnO nanoparticles, while minimizing environmental impact compared to conventional chemical approaches. The extracts were prepared following a standardized protocol, and their phytochemical profiles, including total phenolics, flavonoids, and antioxidant capacity, were quantified via UV-Vis spectroscopy to confirm their reducing potential. ZnO nanoparticles were synthesized using zinc acetate dihydrate as a precursor, with variations in pH and precursor concentration in both aqueous and ethanolic media. UV-Vis spectroscopy confirmed nanoparticle formation, while X-ray diffraction (XRD) revealed a hexagonal wurtzite structure with preferential (101) orientation and lattice parameters a = b = 3.244 Å, c = 5.197 Å. Scanning electron microscopy (SEM) showed agglomerated morphologies, and Fourier transform infrared spectroscopy (FTIR) confirmed the presence of phytochemicals such as quercetin, kaempferol, saponins, and terpenes, along with Zn–O bonding, indicating surface functionalization. Zeta potential measurements showed improved dispersion under alkaline conditions, particularly with ethanolic extracts. This study presents a sustainable synthesis strategy with tunable parameters, highlighting the critical influence of precursor concentration and solvent environment on ZnO nanoparticle formation. Notably, aqueous extracts promote ZnO synthesis at low precursor concentrations, while alkaline conditions are essential when using ethanolic extracts. Compared to other green synthesis methods, this strategy offers control and reproducibility and employs a non-toxic, underexplored plant source rich in phytochemicals, potentially enhancing the crystallinity, surface functionality, and application potential of the resulting ZnO nanoparticles. These materials show promise for applications in photocatalysis, in antimicrobial coatings, in UV-blocking formulations, and as functional additives in optoelectronic and environmental remediation technologies.