Direct laser writing (DLW) is a convenient approach for fabricating graphene-based flexible electronic devices. In this paper, laser-induced graphene was successfully prepared on a thin and transparent polyimide film through the DLW process. Experiments have demonstrated that interdigital thin film capacitor prepared by the DLW method has a high specific capacitance of 8.11 mF/cm² and volume capacitance density of 3.16 F/cm³ (0.05 mA/cm²) due to the doped fluoride in the laser-induced graphene. The capacitance is about 20 times larger than the super-capacitor based non-transparent polyimide film of the same thickness. Owing to its thin, flexible, higher electrochemical characteristics, the transparent polyimide film is promising for integrating and powering portable and wearable electronics.

CdTe quantum dots (QDs) are attractive photosensitizers for photocatalytic proton reduction due to their broad absorbance profile that can extend from the ultraviolet to near-infrared regions, providing access to a larger portion of the solar spectrum than possible with analogous CdSe and CdS QD photosensitizers. Here, the photocatalytic hydrogen (H₂) generation from various sizes of dihydrolipoic acid (DHLA)-capped CdTe QDs, ranging from 2.5 to 7.5 nm in diameter, and a molecular Ni-DHLA catalyst in aqueous solutions was evaluated, and an unusual size-dependent photocatalytic activity with CdTe QDs was observed. Under optimized conditions, using 3.4 nm CdTe-DHLA and a 1:20 ratio of QD/Ni-DHLA catalyst, as many as 38 000 turnover numbers (mol H₂ per mol QD) were achieved. However, below this critical size, the H₂ production efficiency decreased; this behavior is attributed to the rapid oxidation of the QD surface, resulting in detrimental surface trap states. These results are consistent with ultrafast transient absorption spectroscopic measurements, which suggest the presence of extremely fast charge-trapping processes in the oxidized CdTe-DHLA QDs. While fast electron transfer from CdTe-DHLA QDs is observed in the presence of the Ni-DHLA catalyst, the charge trapping processes occur on a competitive time scale, thus lowering the efficiency of the CdTe/Ni-DHLA H₂ production system. Understanding rapid charge trapping in CdTe QDs may help suggest potential improvements for the overall CdTe photocatalytic system.

Polyimide membranes have excellent physiochemical properties which make them valuable materials for optical area. However, common aromatic polyimide membrane trend to show low transmittance in visible region because of the charge-transfer complex (CTC) in molecular structures. Moreover, it’s trending to show high moisture uptakes because of the hydrophilic imide rings in molecular structure. In this work, a polyimide composite membrane with SiO₂ antireflective membrane on both sides was prepared. High transmittance (93% within 500~800 nm) and surface hydrophobicity was realized simultaneously. The polyimide composite membrane showed great optical homogeneity. The SiO₂ antireflective membranes on polyimide substrate were prepared through a simple and efficient sol-gel method. The surface roughness of polyimide membrane substrate on each side has been improved to 1.56 nm and 3.14 nm, respectively. Moreover, the excellent thermal stability and mechanical property of polyimide membrane has been preserved, which greatly improves the range of applications for the composite membrane. It is a good candidate for light weight optical system.

Polyimide diffractive membrane lens can be used in space optical telescope to reduce the size and mass of an imaging system. However, traditional commercial aromatic polyimide membrane is hard to meet the challenging requirements of dimensional stability and optical homogeneity for optical use. Based on molecular structure design and the optimization of fabrication process, the prepared copolyamide-imide membrane achieved the desired performance of membrane as an optical material. It showed a very low coefficient of thermal expansion (CTE), which is 0.95 ppm/°C over a temperature range of −150–100 °C and relatively low coefficient of moisture expansion (CME), which is only 13.30 ppm/% RH (0~90% RH). For the optical use, the prepared copolyamide-imide membrane (φ200 mm) achieved good thickness uniformity with wave-front error smaller than λ/30 (λ = 632 nm) in RMS (root mean square). Besides, it simultaneously meets the optical, thermal, and mechanical requirements for space telescope use. Copolyamide-imide membranes in this research with good comprehensive performance can be used as large aperture membrane optical system architectures.

ZnSe nanorod films grown on fused quartz glass substrates via a simple two-step synthesis protocol were demonstrated to be environmentally safe and effective recyclable photocatalysts. These films showed greatly enhanced photocatalytic activity compared to pulsed laser deposition ZnSe films in the degradation of methyl orange dye solutions. The well-crystalized ZnSe nanorods had a length of 15 µm and a diameter of 200 nm and were densely grown on the substrate. The morphology, crystal structure, crystal phase, and photophysical properties of the ZnSe nanorod films were investigated using field-emission scanning electron microscopy (FE-SEM), UV-Vis spectroscopy, X-ray diffraction (XRD), transmission electron microscopy (TEM), and high resolution transmission electron microscopy (HRTEM).

Hexagonal ZnSe nanowires were synthesized by the self-assembly of nanoparticles prepared by femtosecond laser ablation in deionized water. With introduction of air, partially hollow ZnSe nanotubes were also obtained. The nature of the ZnSe nanowires was characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectrometry mapping (EDS-Mapping), and X-ray diffraction (XRD). Possible self-assembly and hydrolysis mechanisms for the formation of nanowires and partially hollow nanotubes were discussed.