Propane dehydrogenation (PDH) to propene is an important alternative to oil-based cracking processes, to produce this industrially important platform chemical^1,2. The commercial PDH technologies utilizing Cr-containing (refs. ^3,4) or Pt-containing (refs. ^5–8) catalysts suffer from the toxicity of Cr(vi) compounds or the need to use ecologically harmful chlorine for catalyst regeneration⁹. Here, we introduce a method for preparation of environmentally compatible supported catalysts based on commercial ZnO. This metal oxide and a support (zeolite or common metal oxide) are used as a physical mixture or in the form of two layers with ZnO as the upstream layer. Supported ZnO_x species are in situ formed through a reaction of support OH groups with Zn atoms generated from ZnO upon reductive treatment above 550 °C. Using different complementary characterization methods, we identify the decisive role of defective OH groups for the formation of active ZnO_x species. For benchmarking purposes, the developed ZnO–silicalite-1 and an analogue of commercial K–CrO_x/Al₂O₃ were tested in the same setup under industrially relevant conditions at close propane conversion over about 400 h on propane stream. The developed catalyst reveals about three times higher propene productivity at similar propene selectivity.

The surface electron density significantly affects the photocatalytic efficiency, especially the photocatalytic CO₂ reduction reaction, which involves multi-electron participation in the conversion process. Herein, we propose a conceptually different mechanism for surface electron density modulation based on the model of Au anchored CdS. We firstly manipulate the direction of electron transfer by regulating the vacancy types of CdS. When electrons accumulate on vacancies instead of single Au atoms, the adsorption types of CO₂ change from physical adsorption to chemical adsorption. More importantly, the surface electron density is manipulated by controlling the size of Au nanostructures. When Au nanoclusters downsize to single Au atoms, the strong hybridization of Au 5d and S 2p orbits accelerates the photo-electrons transfer onto the surface, resulting in more electrons available for CO₂ reduction. As a result, the product generation rate of Au_SA/Cd_1−xS manifests a remarkable at least 113-fold enhancement compared with pristine Cd_1−xS.

MoO_3−x displayed dramatically enhanced photo-thermal synergistic CO₂ reduction under simulate sunlight irradiation compared to MoO₃ due to the LSPR of MoO_3−x triggered by oxygen vacancies.