Carbon nanotubes (CNTs) have been under scientific investigation for more than fifteen years because of their unique properties that predestine them for many potential applications. The field of nanotechnology and nanoscience push their investigation forward to produce CNTs with suitable parameters for future applications. It is evident that new approaches of their synthesis need to be developed and optimized. In this paper we review history, types, structure and especially the different synthesis methods for CNTs preparation including arc discharge, laser ablation and chemical vapour deposition. Moreover, we mention some rarely used ways of arc discharge deposition which involves arc discharge in liquid solutions in contrary to standard used deposition in a gas atmosphere. In addition, the methods for uniform vertically aligned CNTs synthesis using lithographic techniques for catalyst deposition as well as a method utilizing a nanoporous anodized aluminium oxide as a pattern for selective CNTs growth are reported too.

Graphite oxide has been investigated as a possible room-temperature chemiresistive sensor of ammonia in a gas phase. Graphite oxide was synthesized from high purity graphite using the modified Hummers method. The graphite oxide sample was investigated using scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, thermogravimetry and differential scanning calorimetry. Sensing properties were tested in a wide range of ammonia concentrations in air (10–1000 ppm) and under different relative humidity levels (3%–65%). It was concluded that the graphite oxide–based sensor possessed a good response to NH₃ in dry synthetic air (ΔR/R₀ ranged from 2.5% to 7.4% for concentrations of 100–500 ppm and 3% relative humidity) with negligible cross-sensitivity towards H₂ and CH₄. It was determined that the sensor recovery rate was improved with ammonia concentration growth. Increasing the ambient relative humidity led to an increase of the sensor response. The highest response of 22.2% for 100 ppm of ammonia was achieved at a 65% relative humidity level.

Sensors based on multi-walled carbon nanotubes (MWCNTs) were functionalized by oxygen plasma treatment and plasma co-polymerization of maleic anhydride and acetylene, obtaining core-shell carbon nanopartices covered by functional groups. The active nanostructured carbonaceous material was investigated by scanning electron microscopy, energy dispersive X-ray spectroscopy, Raman spectroscopy and X-ray photoelectron spectroscopy. It was confirmed that plasma treatment increases the content of surface functional groups. The sensing properties of the functionalized material were measured in the range of 10-1000 ppm of NH3 at room temperature. The plasma treated sensor showed an extremely high response of 22.5 %, 27.9 % and 31.4 % to 100 ppm, 250 ppm and 500 ppm of NH3, respectively. It was shown that the nature of NH3 adsorption on the surface of functionalized nanostructured carbon material is physical adsorption.

Vertically aligned multi-walled carbon nanotubes (VA-MWCNTs) with an average diameter below 80 nm and a thickness of the uniform VA-MWCNT layer of about 16 µm were grown in microwave plasma torch and tested for selected functional properties. IR absorption important for a construction of bolometers was studied by Fourier transform infrared spectroscopy. Basic electrochemical characterization was performed by cyclic voltammetry. Comparing the obtained results with the standard or MWCNT‑modified screen-printed electrodes, the prepared VA-MWCNT electrodes indicated their high potential for the construction of electrochemical sensors. Resistive CNT gas sensor revealed a good sensitivity to ammonia taking into account room temperature operation. Field emission detected from CNTs was suitable for the pressure sensing application based on the measurement of emission current in the diode structure with bending diaphragm. The advantages of microwave plasma torch growth of CNTs, i.e., fast processing and versatility of the process, can be therefore fully exploited for the integration of surface-bound grown CNTs into various sensing structures.