Two series of Ni/Ce(Ti/Nb)ZrO₂ catalysts were prepared using citrate route and original solvothermal continuous flow synthesis in supercritical isopropanol and studied in dry reforming of methane (DRM). TEM, XPS and FTIRS of adsorbed CO confirm influence of support composition and preparation method on the catalysts’ morphology and surface features. The oxygen mobility was studied by isotope heteroexchange with C¹⁸O₂. After testing in DRM, carbon deposits after catalysts’ testing in DRM were investigated by temperature-programmed oxidation with thermo-gravimetric analysis. The lowest amounts of carbon deposits were obtained for unmodified Ni-CeZr and Ni-CeNbZr compositions. Ti addition lead to an increased amount of carbon, which was removed at higher temperatures. The use of supercritical supports also resulted in the formation of a higher amount of coke. Catalysts prepared by the supercritical synthesis were tested in DRM for 25 h. The highest activity drop was observed in the first three hours. For all compositions, close values of carbon deposits were revealed.

Nickel-containing mixed ceria-zirconia oxides also doped by Nb and Ti have been prepared by a citrate route and by original solvothermal continuous flow synthesis in supercritical alcohols. Nickel was subsequently deposited by conventional insipient wetness impregnation. The oxides are comprised of ceria-zirconia solid solution with cubic fluorite phase. Negligible amounts of impurities of zirconia are observed for samples prepared by citrate route and doped by Ti. Supports prepared by supercritical synthesis are single-phased. XRD data, Raman, and UV-Vis DR (diffuse reflectance) spectroscopy suggest increasing lattice parameter and amount of oxygen vacancies in fluorite structure after Nb and Ti incorporation despite of the preparation method. These structural changes correlate with the catalytic activity in a methane dry reforming reaction. Catalysts synthesized under supercritical conditions are more active than the catalysts of the same composition prepared by the citrate route. The catalytic activity of samples doped with Ti and Nb is two times higher in terms of TOF (turnover frequency) and increased stability of these catalysts is attributed with the highest oxygen mobility being crucial for gasification of coke precursors.

The Ni-containing catalysts based on ceria–zirconia doped with Ti and Ti+Nb were prepared by the solvothermal method in supercritical fluids. Ni deposition was carried out by incipient wetness impregnation and the one-pot technique. All materials were investigated by a complex of physicochemical methods (XRD, BET, TEM, H₂-TPR). Samples catalytic properties were studied in methane dry reforming in the plug-flow reactor. Conversions of CH₄ and CO₂, H₂/CO ratio, and CO and H₂ yields were measured, and detailed kinetics analysis was carried out. The influence of Ni loading method and support modification on the catalytic behavior in the methane dry reforming process was studied. The preparation method of catalysts affects the textural characteristics. For one-pot samples, pore volume and surface area are lower than for impregnated samples. For catalysts on modified supports, strong metal–support interaction was shown to increase catalytic activity. A reduction pretreatment of samples was shown to have significant influence on their catalytic properties. The kinetic parameters such as reaction rate constant at 700 °C, effective activation energy, and TOF were estimated and analyzed.

To achieve a high activity and coking stability of nickel catalysts in dry reforming of methane, materials comprised of ceria–zirconia doped by Ti were investigated as supports. Ceria–zirconia supports doped with titanium were prepared either via the Pechini method or by synthesis in supercritical alcohol media. Ni-containing catalysts were prepared by two techniques: standard incipient wetness impregnation and one-pot synthesis. The catalytic reaction of DRM to synthesis gas was carried out in the 600–750 °C range over 5% wt. Ni/Ce(Ti)ZrO₂. Dried and calcined supports and catalysts were characterized by physicochemical methods including N₂ adsorption, XRD, Raman, H₂-TPR, and HRTEM. Both preparation methods led to formation of solid solution with cubic fluorite-like structure, as well as after addition of Ti. Introduction of Ti should provide improved oxygen storage capacity and mobility of support oxygen. The highest activity was observed with the catalyst of 5% wt. Ni/Ce_0.75Ti_0.2Zr_0.05O_2−δ composition due to optimized oxide support structure and support oxygen mobility.