Two series of Ni/Ce(Ti/Nb)ZrO₂ catalysts were prepared using citrate route and original solvothermal continuous flow synthesis in supercritical isopropanol and studied in dry reforming of methane (DRM). TEM, XPS and FTIRS of adsorbed CO confirm influence of support composition and preparation method on the catalysts’ morphology and surface features. The oxygen mobility was studied by isotope heteroexchange with C¹⁸O₂. After testing in DRM, carbon deposits after catalysts’ testing in DRM were investigated by temperature-programmed oxidation with thermo-gravimetric analysis. The lowest amounts of carbon deposits were obtained for unmodified Ni-CeZr and Ni-CeNbZr compositions. Ti addition lead to an increased amount of carbon, which was removed at higher temperatures. The use of supercritical supports also resulted in the formation of a higher amount of coke. Catalysts prepared by the supercritical synthesis were tested in DRM for 25 h. The highest activity drop was observed in the first three hours. For all compositions, close values of carbon deposits were revealed.

This paper reports the results of a study of a water–gas shift reaction over nickel–ceria catalysts with different metal loading. Within this study, the overall CO conversion and observed kinetic behavior were investigated over the temperature range of 250–550 °C in different reactor configurations (fixed-bed and microchannel reactors). The quasi-steady state kinetics of the CO water–gas shift reaction was studied for fractions of Ni-containing cerium oxide catalysts in fixed-bed experiments at lab-scale level using a very dilute gas (1% CO + 1.8% H₂O in Не). A set of experiments with a microchannel reactor was performed using the feed composition (CO:H₂O:H₂:N₂ = 1:2:2:2), representing a product gas from methane partial oxidation. The results were interpreted using computational models. The kinetic parameters were determined by regression analysis, while mechanistic aspects were considered only briefly. Simulation of the WGS reaction in the microreactor was also carried out by using the COMSOL Multiphysics program.

Nickel-containing mixed ceria-zirconia oxides also doped by Nb and Ti have been prepared by a citrate route and by original solvothermal continuous flow synthesis in supercritical alcohols. Nickel was subsequently deposited by conventional insipient wetness impregnation. The oxides are comprised of ceria-zirconia solid solution with cubic fluorite phase. Negligible amounts of impurities of zirconia are observed for samples prepared by citrate route and doped by Ti. Supports prepared by supercritical synthesis are single-phased. XRD data, Raman, and UV-Vis DR (diffuse reflectance) spectroscopy suggest increasing lattice parameter and amount of oxygen vacancies in fluorite structure after Nb and Ti incorporation despite of the preparation method. These structural changes correlate with the catalytic activity in a methane dry reforming reaction. Catalysts synthesized under supercritical conditions are more active than the catalysts of the same composition prepared by the citrate route. The catalytic activity of samples doped with Ti and Nb is two times higher in terms of TOF (turnover frequency) and increased stability of these catalysts is attributed with the highest oxygen mobility being crucial for gasification of coke precursors.