The aim of this study was to investigate the cytocompatibility and mineralization potential of two premixed hydraulic endodontic sealers compared with an epoxy resin-based root canal sealer. The cellular responses and mineralization capacity were studied in human periodontal ligament stem cells (hPDLSCs) that were exposed to premixed hydraulic sealers, Bio-C Sealer (Angelus, Londrína, PR, Brazil), TotalFill BC Sealer (FKG Dentaire SA, La-Chaux-de-fonds, Switzerland) and an epoxy resin-based material, AH Plus (Dentsply De Trey, Konstanz, Germany). Non-exposed cultures served as the control. The endodontic sealers were assessed using scanning electron microscopy (SEM) and energy dispersive X-ray microanalysis (EDX). Statistical analyses were done using Analisis of Variance (ANOVA), with Bonferroni adjusted pairwise comparison (p = 0.05). AH Plus reduced cell viability and cell migration, whereas increased cell viability and cell migration were observed in the Bio-C Sealer and the TotalFill BC Sealer (p < 0.05). The lowest cell attachment and spreading were observed for all concentrations of AH Plus, whereas the highest were observed for TotalFill BC Sealer. At the end of 21 days, only the Bio-C Sealer and the TotalFill BC Sealer supported matrix mineralization (p < 0.05). Additionally, SEM-EDX revealed high content of calcium, oxygen, and silicon in the Bio-C Sealer and the TotalFill BC Sealer. Based on the results from this study, Bio-C Sealer and TotalFill BC Sealer demonstrated better cytocompatibility in terms of cell viability, migration, cell morphology, cell attachment, and mineralization capacity than AH Plus.

Biocompatibility is an essential property for any vital pulp material that may interact with the dental pulp tissues. Accordingly, this study aimed to compare the chemical composition and ultrastructural morphology of Biodentine (Septodont, Saint Maur-des-Fosses, France), ProRoot MTA (Dentsply Tulsa Dental Specialties, Johnson City, TN, USA), and Bio-C Repair (Angelus, Londrina, PR, Brazil), as well as their biological effects on human dental pulp cells. Chemical element characterization of the materials was undertaken using scanning electron microscopy and energy dispersive X-ray analysis (SEM-EDX). The cytotoxicity was assessed by analyzing the cell viability (MTT assay), cell morphology (immunofluorescence assay), and cell attachment (flow cytometry assay). The results were statistically analyzed using ANOVA and Tukey’s test (p < 0.05). EDX revealed that ProRoot MTA and Biodentine were mostly composed of calcium, carbon, and oxygen (among others), whereas Bio-C Repair evidenced a low concentration of calcium and the highest concentration of zirconium. SEM showed adequate attachment of human dental pulp cells (hDPCS) to vital pulp materials and cytoskeletal alterations were not observed in the presence of material eluates. Remarkably, the undiluted Biodentine group showed higher viability than the control group cells (without eluates) at 24 h, 48 h, and 72 h (p < 0.001). Based on the evidence derived from an in vitro cellular study, it was concluded that Bio-C Repair showed excellent cytocompatibility that was similar to Biodentine and ProRoot MTA.

Background: The aim of this study was: to evaluate the biological properties of new hydraulic materials: Bio-C Repair and Bio-C Sealer. Methods: Periodontal ligament stem cells were exposed to several dilutions of Bio-C Repair and Bio-C Sealer. The ion release profile and pH were determined. Metabolic activity, cell migration and cell survival were assessed using the 3-(4, 5-dimethylthiazol-2-yl)-2, 5-diphenyltetrazolium bromide (MTT), wound-healing assays and Annexin assays, respectively. Cells were cultured in direct contact with the surface of each material. These were then analyzed via scanning electron microscopy (SEM) and energy dispersive X-ray (EDX). Statistical differences were assessed using a two-way ANOVA (α < 0.05). Results: Similar pH was observed in these cements. Bio-C Sealer released significantly more Ca and Si ions (p < 0.05) in comparison with Bio-C Repair. Undiluted Bio-C Sealer induced a significant reduction on cellular viability, cell survival and cell migration when compared to the control (p < 0.05). Moreover, SEM showed abundant cells adhered on Bio-C Repair and a moderate number of cells attached on Bio-C Sealer. Finally, EDX analysis identified higher percentages of Ca and O in the case of Bio-C repair than with Bio-C sealer, while other elements such as Zr and Si were more abundant in Bio-C sealer. Conclusions: Bio-C Repair displayed higher cell viability, cell adhesion and migration rates than Bio-C Sealer.

Dentinal tubule penetration influences root canal treatment sealing. The aim of this study was to compare dentinal penetration of two clinical presentations of silicate-based sealers using confocal laser. Sixty single-rooted human teeth from 50–70 year-old patients extracted for orthodontic/periodontal reasons were used. Canals were prepared using Mtwo system up to 35/0.04, with 5.25% NaOCl irrigation and final irrigation using 17% EDTA. Teeth were randomly assigned into study groups (n_i = 20): EndoSequence BC sealer (ES, group 1), BioRoot RCS (BR, group 2); and a control group (n_c = 20) with AH Plus (AHP). Root canals were obturated with 35/0.04 gutta-percha (single-cone technique). The samples were obtained from apical, middle, and coronal thirds. Dentinal tubule penetration depth and percentage of penetration around the canal perimeter were measured. The statistical analysis was performed using Mann Whitney U test and Wilcoxon t-test (95% confidence interval). ES exhibited a significantly higher penetration than AHP in apical and middle thirds (p < 0.05), and in middle and coronal thirds relative to BR (p < 0.05). The percentage of penetration around the canal perimeter was significantly higher for ES compared to BR in all thirds, but only in the apical third for AHP (p < 0.05). The pre-mixed silicate-based sealer exhibited better penetration than the powder/liquid one.

New bioactive materials have been developed for retrograde root filling. These materials come into contact with vital tissues and facilitate biomineralization and apical repair. The objective of this study was to evaluate the cytocompatibility and bioactivity of two bioactive cements, Bio-C Repair (Angelus, Londrina, Pr, Brazil) and TotalFill BC RRM putty (FGK, Dentaire SA, La-Chaux-de-fonds, Switzerland). The biological properties in human periodontal ligament stem cells (hPDLSCs) that were exposed to Bio-C Repair and TotalFill BC RRM putty were studied. Cell viability, migration, and cell adhesion were analyzed. Moreover, qPCR and mineralization assay were performed to evaluate the bioactivity potential of these cements. The results were statistically analyzed using ANOVA and the Tukey test (p < 0.05). It was observed that cell viability and cell migration in Bio-C Repair and TotalFill BC RRM putty were similar to the control without statistically significant differences, except at 72 h when TotalFill BC RRM putty was slightly lower (p < 0.05). Excellent cell adhesion and morphology were observed with both Bio-C Repair and TotalFill BC RRM putty. Both cements promoted the osteo- and cementogenic differentiation of hPDLSCs. These results suggest that Bio-C Repair and TotalFill BC RRM putty are biologically appropriate materials to be used as retrograde obturation material.

Objectives: To assess the cytocompatibility and bioactive potential of the new calcium silicate-based cement Ceraputty on human periodontal ligament stem cells (hPDLSCs) compared to Biodentine and Endosequence BC root repair material (ERRM). Materials and methods: hPDLSCs were isolated from extracted third molars from healthy donors. Standardized sample discs and 1:1, 1:2, and 1:4 eluates of the tested materials were prepared. The following assays were performed: surface element distribution via SEM–EDX, cell attachment and morphology via SEM, cell viability via a MTT assay, osteo/cemento/odontogenic marker expression via RT-qPCR, and cell calcified nodule formation via Alizarin Red S staining. hPDLSCs cultured in unconditioned or osteogenic media were used as negative and positive control groups, respectively. Statistical analysis was performed using one-way ANOVA or two-way ANOVA and Tukey’s post hoc test. Statistical significance was established at p < 0.05. Results: The highest Ca²⁺ peak was detected from Biodentine samples, followed by ERRM and Ceraputty. hPDLSC viability was significantly reduced in Ceraputty samples (p < 0.001), while 1:2 and 1:4 Biodentine and ERRM samples similar results to that of the negative control (p > 0.05). Biodentine and ERRM exhibited an upregulation of at least one cemento/odonto/osteogenic marker compared to the negative and positive control groups. Cells cultured with Biodentine produced a significantly higher calcified nodule formation than ERRM and Ceraputty (p < 0.001), which were also higher than the control groups (p < 0.001). Conclusion: Ceraputty evidenced a reduced cytocompatibility towards hPDLSCs on its lowest dilutions compared to the other tested cements and the control group. Biodentine and ERRM promoted a significantly higher mineralization and osteo/cementogenic marker expression on hPDLSCs compared with Ceraputty. Further studies are necessary to verify the biological properties of this new material and its adequacy as a retrograde filling material. Clinical relevance: This is the first study to elucidate the adequate biological properties of Ceraputty for its use as a retrograde filling material.