This research aims to study the spinnability of pristine PALF and PALF blended cotton using the existing spinning machines. Apron draft ring spinning frame and flyer jute spinning frame were used to produce 100% PALF yarn and the yarns count were found 121 tex and 138 tex separately. Besides, 90:10 and 80:20 cotton-PALF blended 30 tex yarn spun in a cotton spinning system with different twist factors. With both yarns, two samples; 1/1 plain and 3/1 twill fabrics, were fabricated through equal density. For plain and twill fabric, PALF yarn of 121 tex and 138 tex were used in the warp way, respectively and PALF blended cotton yarn of 60 tex was used in the weft way. Through the study, physio-mechanical properties of the samples were explored and FTIR & XRD patterns were analyzed to perform the task for diversified use as an ultimate fiber in industrial and domestic purposes.

The aim of this study was to investigate and compare the effect of process variables on the color and physical characteristics of viscose and cotton knitted fabrics. The effect of dye concentration, salt concentration, soda ash, dyeing time, dyeing temperature, material to liquor ratio, different dye class, fabric GSM, washing time, washing temperature, and enzyme concentration were investigated in terms of color strength (K/S value), color fastness, and pilling resistance. The K/S value of the colored fabric was calculated using UV visible spectrophotometer SF 650 TM and the pilling resistance of the enzyme-treated fabrics was tested by an ICI pilling tester. The results show that dye concentration has the greatest and key effect on the K/S value of viscose and cotton fabric. However, viscose fabric shows a higher K/S value than that of cotton fabric in similar dyeing conditions. Furthermore, the multi-functional dyes demonstrate the upmost K/S value than the vinyl sulphone dyes. Moreover, it was found that enzymatic treatment improved the pilling grade of cotton fabric, whereas no enzymatic effect on viscose fabric was observed.

This study aimed to investigate the effect of extensibility on cotton blended polyester-spandex core-spun yarn in the weft direction of 3/1 right-handed Z-twill denim. For the preparation of samples, 100% ring spun cotton yarn of 42 tex (14^s/1 Ne) was used as warp, and 70:30, 30:70, 60:40, and 40:60 cotton-polyester core-spun yarn of 30 tex (20^s/1) was used in the weft direction. Four categories of denim fabric were fabricated by using the air-jet weaving machine. Spandex yarn was used as a core material of weft with a percentage of 2%, 2.5%, 1.9%, and 1.8% respectively. Different physio-mechanical characteristics namely tensile and tearing strength, GSM, growth and recovery percentage, initial modulus, bending length, drape co-efficiency, abrasion resistance, flexural rigidity were evaluated to justify the quality of fabricated pieces of denim. Water wicking and breathability were taken into consideration when determining comfort. Higher cotton containing specimens exhibited lower tensile and tearing strength. Additionally, the produced denim fabrics showed balanced drapability and good breathability.

A huge amount of waste was generated from the apparel industries. This study aims to develop the process of producing recycled yarn from apparel waste. The apparel leftover fabric was converted to fiber, and the fiber was mixed with virgin cotton in different ratios to produce sustainable 6/1 Ne rotor yarn. The produced yarn qualities viz. count strength product (CSP), elongation percentage, total quality index (TQI) and tenacity were decreased linearly, and opposite scenario observed for thick and thin places, neps, imperfection index (IPI) and hairiness (H) attributes with increasing the amount of waste addition with virgin cotton. The leftover fabric (LOF) can be utilized to develop a sustainable yarn and to zero waste management.

This work investigated the effect of superheated steam (SHS) jute fiber and poly (lactic acid) (PLA) having a weight proportion of 30:70 which were synthesized using the melt blending method. The goal of this treatment was to boost up the fiber-polymer interfacial linkage. The action was conducted in a superheated steam oven at various times (30–120 min) and temperatures (170–220 °C). The biocomposites were assessed in terms of mechanical characteristics, dimensional stability and morphological properties. Compared to different treatment temperatures, the results showed that treatment at 210 °C for 60 min offered the best tensile characteristics. Because of the presence of SHS-Jute, the tensile, impact, bending and dimensional stability of the bio-composites have been improved. The FTIR and SEM study revealed progress in the interfacial linkage between SHS-Jute and PLA. This interfacial link improves the bending strength of SHS-Jute-PLA biocomposites by about 15.64%. X-ray diffraction (XRD) investigation also showed an elevation in the crystalline structure with the incorporation of SHS-Jute. The degradation tests of the biocomposite were carried out in deionized water. SHS treatment reduces hemicellulose contents in jute fiber which causes water uptake% reduction is 54% in SHS-Jute-PLA. The SHS-Jute-PLA biocomposite appeared with promising characteristics for utilization as a green and ecological substitute particle board material.