Studies on chemical precipitation of the calcium orthophosphates have shown that their phase compositions do not vary depending on molar ratio Ca/P but are sensitive to solutions acidity and temperature. These are two key factors that determine the phase transformation progress of metastable phases into less soluble precipitates of the phosphates. It was proposed to compare calcium orthophosphates solubility products with calcium cations quantities in their formulas. It was found that there was a linear correlation between calcium orthophosphates specific solubility products and their molar ratios Ca/P if hydroxyapatite and its Ca-deficient forms were excluded from consideration. It was concluded that the relatively large deviations of their solubility products from the found correlation should be thought of as erroneous data. That is why solubility products were changed in accordance with correlation dependence: pK_S for hydroxyapatite was 155, pK_S for Ca-deficient hydroxyapatites was 114–155. The solubility isotherms, which were calculated on the basis of the corrected pK_S values, coincided with the experimental data on solid-phase titration by Pan and Darvell.

A two-component interfacial layer model was employed to describe the experimental results obtained for various surfactants. In contrast to the previous works, here it is shown that the adsorption activity of alkane depends on its interaction with the adsorbed surfactant, and is proportional to the surface coverage by this surfactant. Also, it is assumed that this increase of the adsorption activity parameter is limited by some maximum value. This model provides a good description of the influence of hexane and dodecane which results in the decrease of surface tension by 2-5 mN/m at very low surfactant concentrations. The adsorbed amounts of the surfactant and alkane molecules in this low surfactant concentration range are determined. The adsorbed amounts of the surfactant and alkane molecules in this low surfactant concentration range have been calculated. The reorientation model of surfactant adsorption predicts a smaller number of alkane molecules per one surfactant molecule than that which follows from the Frumkin model.

The method of iodometric determination of chlorates impurities in sodium hypochlorite solutions for medical and veterinary purposes was developed. This method does not require sophisticated equipment and can be implemented directly where the solutions are used. The method is based on the different rates of interaction of ClO^- and ClO3- with iodide ions depending on the acidity of the medium. We have shown that blank titration is advisable to improve the accuracy of the determination of low concentrations of chlorates in the matrix of hypochlorite which is present in excess since in this case possible systematic errors due to the presence of oxidizing impurities in the reagents are prevented. To quantify the low concentrations of chlorates, we proposed to remove 85-95% of hypochlorite ions by means of reducing their excess with sodium sulfite at pH 10.5. The solution of sodium sulfite does not require standardization before each analysis in the proposed procedure. The possibility of quantitative determination of chlorate impurities in the range of 2-50 mg/L in the presence of 50-500–fold excess of sodium hypochlorite with an error of 5% has been proved. The expanded uncertainty of chlorate determination did not exceed 0.6 mg/L.

Electrodeposition of lead dioxide in the presence of Nafion in solution is described by a four-stage kinetic scheme. The limiting stage at low polarizations is that of the second-electron transfer,...

Rutile decomposition by sulfuric acid, including the formation of two salts, Ti(SO₄)₂/TiOSO₄, is thermodynamically modelled. It is shown that TiO₂ can spontaneously dissolve in H₂SO₄ solutions. However, titania is considered as an inert (ballast) phase component of titanium-containing raw materials due to the decelerated separate nature of such chemical transformations. It is concluded that the hampered related kinetics of dissolution can be attributed to the lability of Ti(IV) cations/the specific engineered features of the hierarchical crystalline structure. It is suggested that the breaking of Ti–O–Ti bonds without additional mechanical strains in crystal lattice geometry becomes more advantageous when smaller negative anions/fluoride ions can be used. The analysis of sulfate-fluoride extraction leaching of titanium confirmed that a decrease in the Gibbs energy in the presence of F occurs. It is indicated by kinetic research studies that the addition of corrosive sodium reagent (NaF) reduces the activation by 45 kJ/mol, which results in intensification. A mechanism is proposed for the interactions involving the Ti–O–Ti cleavage on the surface/the H₂SO₄-induced Ti dioxide degradation on the sites of defects. Moreover, F acts as a homogeneous/heterogeneous bifunctional catalyst.